Investigation of optical properties of epitaxial yttrium iron garnet films
- Samara State Aerospace University, 34, Moskovskoe shosse, Samara, 443086 (Russian Federation)
In work we investigated yttrium iron garnet epitaxial films with a thickness of 10 µm and 55 µm which were grown on the surface of garnet substrate. Using the polarizing microscopy method the branching domain structure of films was shown with the period of domains 21.5 µm and 42.5 µm. Disappearance of domains at presence of an external magnetic field up to 100 Oe was noted. The optical transmission of films for the polarized beam of HeNe laser is investigated and zero diffraction order and odd diffraction rings orders were shown. Interconnection of the period of chaotically oriented domains with angles of axially symmetric diffraction rings orders was shown. Diffraction patterns at various longitudinal magnetic fields are investigated. Disappearance of odd diffraction orders and increasing in intensity of zero diffraction order were fixed. Optical transmission of epitaxial films was measured in range of 500 - 900 nm.
- OSTI ID:
- 22591064
- Journal Information:
- AIP Conference Proceedings, Vol. 1724, Issue 1; Conference: ETMN-2015: 2. international conference on emerging technologies: Micro to nano 2015, Rajasthan (India), 24-25 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation of the magnetization process of domain walls in an iron-garnet film by direct optical observation of vertical Bloch lines
Thin yttrium iron garnet films grown by pulsed laser deposition: Crystal structure, static, and dynamic magnetic properties