Synthesis of Mg{sub 2}SiO{sub 4}:Dy{sup 3+} nanoparticles by hydrothermal method and investigation of their thermo and photo luminescence properties

Journal Article · Sun May 15 00:00:00 EDT 2016 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2016.01.026· OSTI ID:22581526

Mostafavi, K. ^[1]

---

1. Department of Materials Engineering, Science and Research branch, Islamic Azad University, Tehran (Iran, Islamic Republic of)

Highlights: • Mg{sub 2}SiO{sub 4}:Dy{sup 3+} nanoparticles have been prepared by hydrothermal and combustion methods. • Thermo and photo luminescent behavior of Mg{sub 2}SiO{sub 4}:Dy{sup 3+} was studied. • The effect of synthesis method on TL properties of Mg{sub 2}SiO{sub 4}:Dy{sup 3+} was investigated. • The optimal dopant concentration for thermo-luminescent property was obtained. - Abstract: In this study, photo and thermo-luminescent properties of Nano crystalline Mg{sub 2}SiO{sub 4}:Dy{sup 3+} prepared by a hydrothermal method were studied and compared to those of nanoparticles prepared by combustion method. The synthesized sample was characterized by X-ray diffraction, transmission electron microscopy, scanning electron microscopy and photoluminescence spectroscopy. The effect of Dy concentration on photo and thermoluminescent intensities was studied. The X-ray diffraction (XRD) patterns of the samples revealed that forsterite was formed as a major phase for all the samples. The crystallite size was found to be in the range of 20–50 nm. The thermo luminescent glow curve indicated that the hydrothermal sample was more efficient than the combustion sample. Two prominent TL bands located at 200 nm and 320 nm were recorded. The prepared nanoparticles exhibited a roughly linear dose response to absorbed dose of 1000 Gy received from 60Co gamma source, suggesting that nanomaterial could be a good candidate for high dose dosimetry.

• OSTI ID: 22581526
• Journal Information: Materials Research Bulletin, Vol. 77; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
77 NANOSCIENCE AND NANOTECHNOLOGY
ABSORBED RADIATION DOSES
COBALT 60
COMBUSTION
COMPARATIVE EVALUATIONS
CONCENTRATION RATIO
DOPED MATERIALS
DYSPROSIUM IONS
EMISSION SPECTROSCOPY
GAMMA SOURCES
GLOW CURVE
HYDROTHERMAL SYNTHESIS
NANOMATERIALS
NANOPARTICLES
NANOSTRUCTURES
PHOTOLUMINESCENCE
SCANNING ELECTRON MICROSCOPY
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION