Intense 2.7 μm mid-infrared emission of Er{sup 3+} in oxyfluoride glass ceramic containing NaYF{sub 4} nanocrystals
Highlights: • Transparent oxyfluoride glass-ceramics containing NaYF{sub 4}:Er{sup 3+} nanocrystals have been prepared. • Intense 2.7 μm emission of the glass-ceramics has been demonstrated. • Prolonged decay lifetimes of Er{sup 3+}:{sup 4}I{sub 11/2} and {sup 4}I{sub 13/2} levels have been achieved. - Abstract: Transparent oxyfluoride glass ceramics containing NaYF{sub 4}:Er{sup 3+} nanocrystals have been prepared by melt quenching and subsequent thermal treatment. X-ray diffraction and high-resolution transmission electron microscopy analysis confirmed the precipitation of NaYF{sub 4} nanocrystals in glass. Energy dispersive spectrometer results evidenced the preferential concentration of Er{sup 3+} ions in nanocrystals. Mid-infrared, upconversion, and near-infrared emissions were measured upon excitation with 980 nm laser diode and the luminescence mechanisms were discussed. Intense 2.7 μm emission originating from the Er{sup 3+}:{sup 4}I{sub 11/2} → {sup 4}I{sub 13/2} transition was achieved due to the incorporation of Er{sup 3+} ions into the precipitated low phonon energy fluoride nanocrystals. The results indicate that oxyfluoride glass ceramic containing NaYF{sub 4}:Er{sup 3+} nanocrystals is a promising candidate material for 2.7 μm laser.
- OSTI ID:
- 22581508
- Journal Information:
- Materials Research Bulletin, Vol. 76; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of adjusting composition on the crystallization and luminescence properties in NaYF{sub 4}:Er{sup 3+} embedded glass ceramics
Structural, thermal and spectroscopic properties of highly Er3+-doped novel oxyfluoride glasses for photonic application