Preparation, characterization and millimetre wave attenuation performance of carbon fibers coated with nickel-wolfram-phosphorus and nickel-cobalt-wolfram- phosphorus

Journal Article · Fri Apr 15 00:00:00 EDT 2016 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2015.12.032· OSTI ID:22581502

Ye, Mingquan; Li, Zhitao; Wang, Chen; Han, Aijun

Highlights: • SEM, XRD, EDS and MMW attenuation performances of alloys coated CFs were studied. • Resistivity and P content in alloys were main factors on MMW attenuation property. • The weight gain of coated CFs has effects on the MMW attenuation performance. - Abstract: Carbon fibers (CFs) coated with Ni–X–P (X = W, Co–W or none) alloys were prepared by electroless plating. The morphology, crystal structure, and element composition of alloy-coated CFs were characterized by scanning electron microscopy, X-ray diffractometry, energy-dispersive spectrometry and microwave attenuation. The results showed that CFs were coated with a layer of alloy particles. P content in Ni–Co–W–P or Ni–W–P alloys was lower than that in Ni–P alloy, and coating alloy Ni–P was amorphous. After W or Co introduction, coating alloys exhibited crystal characteristics. MMW-attenuation performance analysis showed that the 3 mm wave attenuation performance of CFs/Ni–Co–W–P, CFs/Ni–W–P and CFs/Ni–P increased by 7.27 dBm, 4.88 dBm and 3.55 dBm, and the 8 mm wave attenuation effects increased by 11.61 dBm, 6.11 dBm, and 4.06 dBm respectively, compared with those of CFs. MMW-attenuation performance is attributable to the sample bulk resistivity and P content in the alloy. Moreover, an optimal weight gain value existed for the MMW-attenuation performance of alloy-coated CFs.

• OSTI ID: 22581502
• Journal Information: Materials Research Bulletin, Vol. 76; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ATTENUATION
CARBON
CARBON FIBERS
COBALT ALLOYS
COMPARATIVE EVALUATIONS
CRYSTAL STRUCTURE
CRYSTALS
LAYERS
MAGNETIC MATERIALS
MICROWAVE RADIATION
NICKEL
NICKEL ALLOYS
PHOSPHORUS ADDITIONS
SCANNING ELECTRON MICROSCOPY
SURFACE PROPERTIES
TUNGSTEN
TUNGSTEN ALLOYS
X-RAY DIFFRACTION
X-RAY SPECTROSCOPY