Temperature induced phase transition of CaMn{sub 0.5}Zr{sub 1.5}(PO{sub 4}){sub 3} phosphate
- Institute of Mineralogy and Petrography, University of Innsbruck, Innrain 52, Innsbruck 6020 (Austria)
- Department of Chemistry, University of Nizhny Novgorod, 23 Gagarin Avenue, Nizhny Novgorod 603950 (Russian Federation)
- CNRS, University of Bordeaux, ICMCB, 87 Albert Schweitzer Avenue, Pessac 33600 (France)
In this work we investigated the structural behaviour of a CaMn{sub 0.5}Zr{sub 1.5}(PO{sub 4}){sub 3}. Due to the presence of divalent Mn{sup 2+} cations this compound can possess interesting luminescence properties. It was recently understood that this phosphate undergoes a temperature induced irreversible phase transition in the range of 800–875 °C. It has also been shown that the 3d–3d luminescence of Mn{sup 2+} increases 10 fold for the high temperature polymorph. To determine the Mn environment structural investigations of both phases have been performed by the X-ray powder diffraction and Raman spectroscopy methods. The low temperature modification adopts the trigonal NZP structure type with a slightly lower symmetry (space group R32, a=8.7850(2) Å, c=22.6496(7) Å, V=1514.8(1) Å{sup 3}). The high temperature form in turn has orthorhombic symmetry (space group Pnma, a=6.2350(3) Å, b=6.6281(3) Å, c=14.4731(6) Å, V=598.13(5) Å{sup 3}). Both structures were solved ab-initio from powder data and structural analysis was performed. In-situ and RT Raman spectra are consistent with the XRD derived structural model. Mn{sup 2+} cations occupy different types of positions in these structures and a change in Mn coordination number (6 for LT phase, 7 for HT phase) results in different Mn–O bond lengths. These differences may explain the change in the optical properties between the polymorphs. - Graphical abstract: The compound CaMn{sub 0.5}Zr{sub 1.5}(PO{sub 4}){sub 3} was synthesized in order to create a material with enhanced luminescent properties. The goal of present studies is to define Mn{sup 2+} environment and its changes due to the structural transformations of the phosphate along phase transition at the T range of 800–875 °C. It was found that LT modification adopts the trigonal NZP structure type, sp.gr. R32, the HT form in turn exhibits orthorhombic symmetry sp.gr. Pnma. Mn2+ cations occupy different types of positions in those structures and a change in coordination number of Mn (6 for LT phase, 7 for HT phase) results in a change in Mn–O bond lengths.
- OSTI ID:
- 22577784
- Journal Information:
- Journal of Solid State Chemistry, Vol. 235; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Phase equilibria in the NaF-CdO-NaPO{sub 3} system at 873 K and crystal structure and physico-chemical characterizations of the new Na{sub 2}CdPO{sub 4}F fluorophosphate
Luminescence, structure and antiferroelectric-type phase transition in Ca8ZnEu(PO4)7