Title: Comparative study of electron transport mechanisms in epitaxial and polycrystalline zinc nitride films

Zn{sub 3}N{sub 2} has been reported to have high electron mobility even in polycrystalline films. The high mobility in polycrystalline films is a striking feature as compared with group-III nitrides. However, the origins of the high mobility have not been elucidated to date. In this paper, we discuss the reason for high mobility in Zn{sub 3}N{sub 2}. We grew epitaxial and polycrystalline films of Zn{sub 3}N{sub 2}. Electron effective mass (m*) was determined optically and found to decrease with a decrease in electron density. Using a nonparabolic conduction band model, the m* at the bottom of the conduction band was derived to be (0.08 ± 0.03)m{sub 0} (m{sub 0} denotes the free electron mass), which is comparable to that in InN. Optically determined intra-grain mobility (μ{sub opt}) in the polycrystalline films was higher than 110 cm{sup 2} V{sup −1} s{sup −1}, resulting from the small m*. The Hall mobility (μ{sub H}) in the polycrystalline films was significantly smaller than μ{sub opt}, indicating that electron transport is impeded by scattering at the grain boundaries. Nevertheless, μ{sub H} higher than 70 cm{sup 2} V{sup −1} s{sup −1} was achievable owing to the beneficial effect of the high μ{sub opt}. As for the epitaxial films, we revealedmore » that electron transport is hardly affected by grain boundary scattering and is governed solely by ionized impurity scattering. The findings in this study suggest that Zn{sub 3}N{sub 2} is a high-mobility semiconductor with small effective mass.« less
Authors:
; ; ;  [1]
  1. Department of Applied Chemistry, Chubu University, 1200 Matsumoto, Kasugai, Aichi 487–8501 (Japan)
Publication Date:
OSTI Identifier:
22494905
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 119; Journal Issue: 2; Other Information: (c) 2016 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; 71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSICS; EFFECTIVE MASS; ELECTRON DENSITY; ELECTRON MOBILITY; EPITAXY; FILMS; GRAIN BOUNDARIES; IMPURITIES; POLYCRYSTALS; SCATTERING; SEMICONDUCTOR MATERIALS; ZINC NITRIDES