The influences of mole composition of strontium (x) on properties of barium strontium titanate (Ba{sub 1−x}Sr{sub x}TiO{sub 3}) prepared by solid state reaction method
- Physics Department, Faculty of Mathematics and Natural Science, Sebelas Maret University (Indonesia)
- Physics Department, Faculty of Teacher Training and Education, Sebelas Maret University (Indonesia)
Barium Strontium Titanate (Ba{sub 1-x}Sr{sub x}TiO{sub 3}) or BST was prepared by solid state reaction method. Raw materials are BaCO{sub 3}, SrCO{sub 3}, and TiO{sub 2}. Those materials are mixed for 8 h, pressed, and sintered at temperature 1200°C for 2 h. Mole composition of Sr (x) was varied to study its influences on structural, morphological, and electrical properties of BST. Variation of (x) are x = 0; x = 0.1; and x = 0.5. XRD patterns showed a single phase of BST, which mean that mixture of raw materials was homogenous. Crystal structure was influenced by x. BaTiO{sub 3} and Ba{sub 0.9}Ti{sub 0.1}TiO{sub 3} have tetragonal crystal structure, while Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} is cubic. The diffraction angle shifted to right side (angle larger) as the increases of x. Crystalline size of BaTiO{sub 3}, Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3}, and Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} are 38.13 nm; 38.62 nm; and 37.13 nm, respectively. SEM images showed that there are still of pores which were influenced by x. Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} has densest surface (pores are few and small in size). Sawyer Tower circuit showed that BaTiO{sub 3} and Ba{sub 0.9}Sr{sub 0.1} TiO{sub 3} is ferroelectric, while Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} is paraelectric. The dielectric constants of BaTiO{sub 3}, Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} and Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} at frequency of 1 KHz are 156; 196; and 83, respectively. Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} has relatively highest dielectric constant. It is considered that Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} has densest surface.
- OSTI ID:
- 22494605
- Journal Information:
- AIP Conference Proceedings, Vol. 1710, Issue 1; Conference: NNS2015: 6. nanoscience and nanotechnology symposium, Surakarta (Indonesia), 4-5 Nov 2015; Other Information: (c) 2016 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characteristics of the surface layer of barium strontium titanate thin films deposited by laser ablation
Synthesis of strontium substituted barium titanate nanoparticles by mechanical alloying and high power ultrasonication destruction
Related Subjects
71 CLASSICAL AND QUANTUM MECHANICS
GENERAL PHYSICS
BARIUM
BARIUM CARBONATES
COOLING TOWERS
CRYSTAL STRUCTURE
FERROELECTRIC MATERIALS
IMAGES
KHZ RANGE 01-100
MIXTURES
PERMITTIVITY
POWER TRANSMISSION TOWERS
PRESSES
RAW MATERIALS
SCANNING ELECTRON MICROSCOPY
SOLIDS
STRONTIUM
STRONTIUM CARBONATES
SURFACES
TITANATES
TITANIUM OXIDES
VARIATIONS
X-RAY DIFFRACTION