Structural and vibrational properties of single crystals of Scandia, Sc{sub 2}O{sub 3} under high pressure
- Bayerisches Geoinstitut, Universität Bayreuth, Universitätsstrasse 30, Bayreuth D-95447 (Germany)
- Deutsches Elektronen-Synchrotron DESY, Notkestrasse 85, D-22603 Hamburg (Germany)
We report the results of single-crystal X-ray diffraction and Raman spectroscopy studies of scandium oxide, Sc{sub 2}O{sub 3}, at ambient temperature under high pressure up to 55 and 28 GPa, respectively. Both X-ray diffraction and Raman studies indicated a phase transition from the cubic bixbyite phase (so-called C-Res phase) to a monoclinic C2/m phase (so-called B-Res phase) at pressures around 25–28 GPa. The transition was accompanied by a significant volumetric drop by ∼6.7%. In addition, the Raman spectroscopy detected a minor crossover around 10–12 GPa, which manifested in the appearance of new and disappearance of some Raman modes, as well as in softening of one Raman mode. We found the bulk modulus values of the both C-Res and B-Res phases as B{sub 0} = 198.2(3) and 171.2(1) GPa (for fixed B′ = 4), respectively. Thus, the denser high-pressure lattice of Sc{sub 2}O{sub 3} is much softer than the original lattice. We discuss possible mechanisms that might be responsible for the pronounced elastic softening in the monoclinic high-pressure phase in this “simple” oxide with an ultra-wide band gap.
- OSTI ID:
- 22492881
- Journal Information:
- Journal of Applied Physics, Vol. 118, Issue 16; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Vibrational spectroscopy and x-ray diffraction of Cd(OH){sub 2} to 28 GPa at 300 K
High-pressure crystallography and compression behavior of the alkali-scandium-germanate end-members LiScGe{sub 2}O{sub 6} and NaScGe{sub 2}O{sub 6}