Electrical properties of GaAs metal–oxide–semiconductor structure comprising Al{sub 2}O{sub 3} gate oxide and AlN passivation layer fabricated in situ using a metal–organic vapor deposition/atomic layer deposition hybrid system
- Sumitomo Chemical Co., Ltd., IT-related Chemicals Research Laboratory, 6 Kitahara, Tsukuba, Ibaraki 300-3294 (Japan)
This paper presents a compressive study on the fabrication and optimization of GaAs metal–oxide–semiconductor (MOS) structures comprising a Al{sub 2}O{sub 3} gate oxide, deposited via atomic layer deposition (ALD), with an AlN interfacial passivation layer prepared in situ via metal–organic chemical vapor deposition (MOCVD). The established protocol afforded self-limiting growth of Al{sub 2}O{sub 3} in the atmospheric MOCVD reactor. Consequently, this enabled successive growth of MOCVD-formed AlN and ALD-formed Al{sub 2}O{sub 3} layers on the GaAs substrate. The effects of AlN thickness, post-deposition anneal (PDA) conditions, and crystal orientation of the GaAs substrate on the electrical properties of the resulting MOS capacitors were investigated. Thin AlN passivation layers afforded incorporation of optimum amounts of nitrogen, leading to good capacitance–voltage (C–V) characteristics with reduced frequency dispersion. In contrast, excessively thick AlN passivation layers degraded the interface, thereby increasing the interfacial density of states (D{sub it}) near the midgap and reducing the conduction band offset. To further improve the interface with the thin AlN passivation layers, the PDA conditions were optimized. Using wet nitrogen at 600 °C was effective to reduce D{sub it} to below 2 × 10{sup 12} cm{sup −2} eV{sup −1}. Using a (111)A substrate was also effective in reducing the frequency dispersion of accumulation capacitance, thus suggesting the suppression of traps in GaAs located near the dielectric/GaAs interface. The current findings suggest that using an atmosphere ALD process with in situ AlN passivation using the current MOCVD system could be an efficient solution to improving GaAs MOS interfaces.
- OSTI ID:
- 22492319
- Journal Information:
- AIP Advances, Vol. 5, Issue 8; Other Information: (c) 2015 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effective passivation of In{sub 0.2}Ga{sub 0.8}As by HfO{sub 2} surpassing Al{sub 2}O{sub 3} via in-situ atomic layer deposition
High-performance self-aligned inversion-channel In{sub 0.53}Ga{sub 0.47}As metal-oxide-semiconductor field-effect-transistors by in-situ atomic-layer-deposited HfO{sub 2}
Related Subjects
ALUMINIUM NITRIDES
ALUMINIUM OXIDES
CAPACITANCE
CHEMICAL VAPOR DEPOSITION
CRYSTALS
DENSITY OF STATES
DEPOSITS
DIELECTRIC MATERIALS
ELECTRIC POTENTIAL
EV RANGE
FABRICATION
GALLIUM ARSENIDES
INTERFACES
LAYERS
NITROGEN
PASSIVATION
SEMICONDUCTOR MATERIALS
SILICON OXIDES
SUBSTRATES
TRAPS