Title: The effect of Tb{sup +3} on α-Sr{sub 2}P{sub 2}O{sub 7} phosphor for green LED phosphor application

A series of Tb{sup +3} activated α-Sr{sub 2}P{sub 2}O{sub 7} (Strontium Pyrophosphate) phosphors were synthesized by high temperature combustion synthesis method. The structural analysis has been done by x-ray diffraction and FTIR (Fourier Transform Infrared Spectrum). The results obtained in structural characterization indicate that the doping concentration did not affect the crystal phase and structure of the phosphors. X-ray diffraction pattern reveals that the all samples were consistence with the JCPDS card No. 24-1011. The phosphor was excited at 232 nm wavelength, very intense PL green emission peak have been observed at 545 nm. This illustrates, that the phosphors could be efficiently excited because of the charge transfer band of the host as well as the energy transfer process occurred between host (Sr{sub 2}P{sub 2}O{sub 7}) and activator (Tb{sup +3}). By increasing the doping concentration of Tb{sup +3}, the intensity of 545 nm emission peak has been increased predominantly and it suggest that the phosphor prepared has very good application in green LED phosphor.
Authors:
; ; ;  [1]
  1. Department of Physics, Faculty of Science, The M. S. University of Baroda, Vadodara-390002 (India)
Publication Date:
OSTI Identifier:
22490504
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1665; Journal Issue: 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; CONCENTRATION RATIO; CRYSTAL STRUCTURE; CRYSTALS; EMISSION; ENERGY TRANSFER; FOURIER TRANSFORMATION; INFRARED SPECTRA; PHOSPHORS; STRONTIUM PHOSPHATES; SYNTHESIS; X-RAY DIFFRACTION