Direct synthesis of Cu{sub 2}O-RGO nanocomposite on Cu foil by thermal evaporation method and its field emission study
- Centre for Advanced Studies in Material Science and Solid State Physics, Department of Physics, University of Pune, Pune-411 007 (India)
In this work, a facile one step thermal evaporation method for deposition of Cu{sub 2}O nanoparticles on RGO sheets to form Cu{sub 2}O-RGO nanocomposite is discussed. To the best of our knowledge, this is the first report on Cu{sub 2}O-RGO nanocomposite, directly grown on Cu foil by a simple thermal evaporation route. The as –prepared nanocomposite exhibits well dispersed Cu{sub 2}O nanoparticles distributed all over the graphene sheet. Field emission properties of the nanocomposite were investigated at a base pressure of 1*10{sup −8} torr. The turn on field, required to draw emission current density of 0.1µA/cm2, was found to be 3.8V/µm with a maximum emission current density of 80 µA/cm2 at an applied field of 6.8 V/µm. Moreover, the nanocomposite shows fairly good emission stability without significant degradation of emission current. The FE results seem to be encouraging, indicative of potential candidature of the Cu{sub 2}O-RGO nanocomposite emitter as an electron source for practical applications in vacuum nanoelectronic devices.
- OSTI ID:
- 22490336
- Journal Information:
- AIP Conference Proceedings, Vol. 1665, Issue 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Inducement of nanoscale Cu–BTC on nanocomposite of PPy–rGO and its performance in ammonia sensing
Effect of Cysteine Substitutions on the Structural and Magnetic Properties of Fe{sub 3}O{sub 4}–Cysteine/RGO and Fe{sub 3}O{sub 4}/RGO–Cysteine Nanocomposites