Oleic acid coated magnetic nano-particles: Synthesis and characterizations
- Pillai’s Institute of Information Technology, Engineering, Media Studies and Research, Dr. K. M. Vasudevan Pillai’s Campus, New Panvel, 410 206 (India)
Magnetic nano particles of Fe{sub 3}O{sub 4} coated with oleic acid were synthesized using wet chemical route, which involved co-precipitation of Fe{sup 2+} and Fe{sup 3+} ions. The nano particles were characterized using XRD, TEM, FTIR, TGA and VSM. X-ray diffraction studies showed that nano particles consist of single phase Fe{sub 3}O{sub 4} having inverse spinel structure. The particle size obtained from width of Bragg peak is about 12.6 nm. TEM analysis showed that sizes of nano particles are in range of 6 to 17 nm with a dominant population at 12 - 14 nm. FTIR and TGA analysis showed that -COOH group of oleic acid is bound to the surface of Fe{sub 3}O{sub 4} particles and one has to heat the sample to 278° C to remove the attached molecule from the surface. Further it was seen that Fe{sub 3}O{sub 4} particles exhibit super paramagnetism with a magnetization of about 53 emu/ gm.
- OSTI ID:
- 22490229
- Journal Information:
- AIP Conference Proceedings, Vol. 1665, Issue 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method
Magnetic properties of nanometer-scale ion particles generated by iron atom clustering in cold pentane
Related Subjects
BRAGG CURVE
COPRECIPITATION
FERRITES
FOURIER TRANSFORMATION
INFRARED SPECTRA
IRON IONS
IRON OXIDES
MAGNETIZATION
OLEIC ACID
PARAMAGNETISM
PARTICLE SIZE
PARTICLES
SPINELS
SURFACES
SYNTHESIS
THERMAL GRAVIMETRIC ANALYSIS
TRANSMISSION ELECTRON MICROSCOPY
VIBRATING SAMPLE MAGNETOMETERS
X-RAY DIFFRACTION