Title: Vanadium dioxide film protected with an atomic-layer-deposited Al{sub 2}O{sub 3} thin film

A VO{sub 2} film exposed to ambient air is prone to oxidation, which will degrade its thermochromic properties. In this work, the authors deposited an ultrathin Al{sub 2}O{sub 3} film with atomic layer deposition (ALD) to protect the underlying VO{sub 2} film from degradation, and then studied the morphology and crystalline structure of the films. To assess the protectiveness of the Al{sub 2}O{sub 3} capping layer, the authors performed a heating test and a damp heating test. An ultrathin 5-nm-thick ALD Al{sub 2}O{sub 3} film was sufficient to protect the underlying VO{sub 2} film heated at 350 °C. However, in a humid environment at prolonged durations, a thicker ALD Al{sub 2}O{sub 3} film (15 nm) was required to protect the VO{sub 2}. The authors also deposited and studied a TiO{sub 2}/Al{sub 2}O{sub 3} bilayer, which significantly improved the protectiveness of the Al{sub 2}O{sub 3} film in a humid environment.
Authors:
; ; ; ;  [1]
  1. Key Laboratory of Inorganic Coating Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 588 Heshuo Road, Shanghai 201800 (China)
Publication Date:
OSTI Identifier:
22489740
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films; Journal Volume: 34; Journal Issue: 1; Other Information: (c) 2015 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 42 ENGINEERING; ALUMINIUM OXIDES; DEPOSITION; DEPOSITS; HEATING; LAYERS; MORPHOLOGY; OXIDATION; THIN FILMS; TITANIUM OXIDES; VANADIUM OXIDES