Effect of irradiation on the prevulcanized latex/low nitrosamines latex blends
Journal Article
·
· AIP Conference Proceedings
- Malaysian Nuclear Agency, 43000 kajang, Selangor (Malaysia)
- Faculty of Science and Technology, Universiti Kebangsaan Malaysia,43600 bangi, Selangor (Malaysia)
Radiation Prevulcanized Natural Rubber Latex (RVNRL) was blended with Low Nitrosamines Latex (LNL) at different composition ratio. Methyl Metachrylate (MMA) was added for grafting onto the blended latex. Blended latex was subjected to gamma irradiation at various doses up to 8kGy. The mechanical properties and FTIR analysis were investigated as a function of the blended composition and irradiation dose. It was found that blending at specific ratio and gamma irradiation at specific dose led to significant improvement on the properties of the latex. The optimum mechanical properties was attained at a total blending ratio of 70% RVNRL and 30% of LNL.
- OSTI ID:
- 22488987
- Journal Information:
- AIP Conference Proceedings, Vol. 1678, Issue 1; Conference: Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2015 Postgraduate Colloquium, Selangor (Malaysia), 15-16 Apr 2015; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Radiation grafting of methyl methacrylate monomer on natural rubber latex. [Gamma radiation]
Preparation of vinyl acetate grafted natural rubber by irradiation method
FORMATION OF GRAFT POLYMERS BY $gamma$-IRRADIATION OF NATURAL RUBBER LATEX AND METHYL METHACRYLATE
Journal Article
·
Tue May 01 00:00:00 EDT 1984
· J. Appl. Polym. Sci.; (United States)
·
OSTI ID:22488987
Preparation of vinyl acetate grafted natural rubber by irradiation method
Journal Article
·
Wed Mar 09 00:00:00 EST 2016
· AIP Conference Proceedings
·
OSTI ID:22488987
FORMATION OF GRAFT POLYMERS BY $gamma$-IRRADIATION OF NATURAL RUBBER LATEX AND METHYL METHACRYLATE
Journal Article
·
Tue Sep 01 00:00:00 EDT 1959
· J. Polymer Sci.
·
OSTI ID:22488987