Title: Lithium ionic mobility study in xLi{sub 2}CO{sub 3}-yLiI (x = 95-70, y = 5-30 wt.%) solid electrolyte by impedance spectroscopy technique

A detailed systematic study on the effects of different amount (wt.%) of LiI addition on the electrical conductivity and dielectric behavior of the xLi{sub 2}CO{sub 3}-xLiI (x = 95-70, y = 5-30 wt.%) electrolyte system was carried out. The samples with different compositions were prepared and ground by mechanical milling method. The electrical and dielectric properties of the samples over a range of frequency (50Hz – 1MHz) were investigated by deploying electrical impedance spectroscopy (EIS) technique in a series of temperature set (298–373K). Normally, Li{sub 2}CO{sub 3} itself shows a very low electrical conductivity (10{sup −5} Scm{sup −1}). However, the electrical conductivity of the system was found to be increased (10{sup −3} Scm{sup −1}) as the lithium salt (LiI) were introduced to the system. The dielectric analysis displayed that the activation energy was inversely proportional to the increment of LiI (wt.%). As the electrical conductivity reached their maximum value (4.63 × 10{sup −3} Scm{sup −1}) at the 20 wt.% of LiI, the activation energy was dropped to the minimum (0.1 eV). The electrical conductivity increases with the temperature (298 – 373K) indicate that the system obeys Arrhenius law.
Authors:
;  [1] ;  [2]
  1. Faculty of Applied Sciences, Universiti Teknologi MARA, 40450 Shah Alam, Selangor D.E. (Malaysia)
  2. (Malaysia)
Publication Date:
OSTI Identifier:
22488770
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1674; Journal Issue: 1; Conference: ICASIT2015: International conference on applied sciences and industrial technology, Negeri Sembilan (Malaysia), 24-26 Feb 2015; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ACTIVATION ENERGY; ARRHENIUS EQUATION; CONCENTRATION RATIO; DIELECTRIC MATERIALS; DIELECTRIC PROPERTIES; ELECTRIC CONDUCTIVITY; EV RANGE; IMPEDANCE; LITHIUM; LITHIUM CARBONATES; MILLING; MOBILITY; SALTS; SOLID ELECTROLYTES; SPECTROSCOPY