Title: Tuning the reactivity of Al/Fe{sub 2}O{sub 3} nanoenergetic materials via an approach combining soft template self-assembly with sol–gel process process

A bottom-up approach combining soft template self-assembly with sol–gel process, was adopted to prepare the assembled Al/Fe{sub 2}O{sub 3} nanoenergetic materials, assembly-Al/Fe{sub 2}O{sub 3} sample. The other two unassembled Al/Fe{sub 2}O{sub 3}a nanoenergetic materials, sol–gel–Al/Fe{sub 2}O{sub 3} sample and mixing-Al/Fe{sub 2}O{sub 3} sample, were prepared by sol–gel method and physical mixing method respectively. The assembly process within the preparation of the assembly-Al/Fe{sub 2}O{sub 3} sample was analyzed through the changes in the average hydrodynamic diameters of the particles and the micelles in solution. SEM, EDS and TEM tests were performed to demonstrate a significant improvement regarding to dispersity and arrangements of the Al and Fe{sub 2}O{sub 3} particles in the assembled samples, compared to that of the unassembled Al/Fe{sub 2}O{sub 3} samples. DSC test was employed to characterize the reactivity of the samples. The heat release of the assembled Al/Fe{sub 2}O{sub 3} sample was 2088 J/g, about 400 and 990 J/g more than that of the sol–gel–Al/Fe{sub 2}O{sub 3} sample and mixing-Al/Fe{sub 2}O{sub 3} sample, respectively. - Graphical abstract: Modified aluminum (Al) nanoparticles with hydrophobic surface assembled into the Brij S10 micelle in Fe(III) sol, then the well dispersed system was transformed into Al/Fe{sub 2}O{sub 3} nanoenergetic materials with highmore » reactivity. - Highlights: • An approach combining soft template self-assembly with sol–gel process was adopted. • The aggregation of Al nanoparticles in the final product was reduced significantly. • The reactivity of Al/Fe{sub 2}O{sub 3} nanoenergetic materials was improved to a large extent.« less
Authors:
; ; ;
Publication Date:
OSTI Identifier:
22486783
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 230; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; 77 NANOSCIENCE AND NANOTECHNOLOGY; AGGLOMERATION; ALUMINIUM; CALORIMETRY; COMPARATIVE EVALUATIONS; FERRITES; HEAT; IRON OXIDES; MIXING; NANOMATERIALS; NANOPARTICLES; REACTIVITY; SCANNING ELECTRON MICROSCOPY; SURFACES; TRANSMISSION ELECTRON MICROSCOPY