Synthesis, characterization, and properties of reduced europium molybdates and tungstates
- Department of Chemistry and Biochemistry, University of South Carolina, Columbia, SC 29208 (United States)
- Institut für Anorganische und Analytische Chemie, Universität Münster , Corrensstrasse 30, Münster D-48149 (Germany)
Single crystals of K{sub 0.094}Eu{sub 0.906}MoO{sub 4}, K{sub 0.097}Eu{sub 0.903}WO{sub 4}, EuWO{sub 4}, and EuMoO{sub 4} were grown from molten chloride fluxes contained in vacuum-sealed fused silica and structurally characterized via single crystal X-ray diffraction. The in situ reduction of Eu{sup 3+} to Eu{sup 2+} was carried out using Mo, W, and Zn as metal reducing agents. All four compounds crystallize in the tetragonal space group of I4{sub 1}/a and adopt the scheelite (CaWO{sub 4}) structure type. The magnetic susceptibility of the reported compounds shows paramagnetic behavior down to 2 K. {sup 151}Eu Mössbauer spectroscopy was used to analyze the relative Eu{sup 2+} and Eu{sup 3+} content of the samples. All the compounds were further characterized by EPR, and UV-vis spectroscopy. - Graphical abstract: TOC Caption Two new reduced europium containing quaternary oxides, K{sub 0.094}Eu{sub 0.906}MoO{sub 4} and K{sub 0.097}Eu{sub 0.903}WO{sub 4}, and two previously reported ternary reduced oxides, EuWO{sub 4} and EuMoO{sub 4}, were synthesized via an in situ reduction of Eu{sup 3+} to Eu{sup 2+} under flux method using Mo, W, and Zn as metal reducing agents. {sup 151}Eu Mössbauer spectroscopy was used to analyze the relative Eu{sup 2+} and Eu{sup 3+} content of the samples. - Highlights: • K{sub 0.094}Eu{sub 0.906}MoO{sub 4}, K{sub 0.097}Eu{sub 0.903}WO{sub 4}, EuWO{sub 4}, and EuMoO{sub 4} have been synthesized and characterized. • The in situ reduction of Eu{sup 3+} to Eu{sup 2+} was carried out using Mo, W, and Zn as metal reducing agents. • Magnetic susceptibility data were collected. • {sup 151}Eu Mössbauer spectroscopy was used to analyze Eu{sup 2+} and Eu{sup 3+} content.
- OSTI ID:
- 22486762
- Journal Information:
- Journal of Solid State Chemistry, Vol. 229; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Valence and magnetism in EuPd3S4 and (Y, La)xEu1-xPd3S4
Structural, spectroscopic and photoluminescence studies of LiEu(WO{sub 4}){sub 2-} {sub x} (MoO{sub 4}) {sub x} as a near-UV convertible phosphor
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ABSORPTION SPECTROSCOPY
CALCIUM TUNGSTATES
CHLORIDES
CRYSTAL GROWTH
ELECTRON SPIN RESONANCE
EUROPIUM 151
EUROPIUM COMPOUNDS
EUROPIUM IONS
MAGNETIC SUSCEPTIBILITY
MOESSBAUER EFFECT
MOLYBDATES
MONOCRYSTALS
PARAMAGNETISM
POTASSIUM COMPOUNDS
REDUCING AGENTS
REDUCTION
SILICA
SYNTHESIS
TETRAGONAL LATTICES
X-RAY DIFFRACTION