Title: Monoclinically distorted perovskites, A{sub 2}ZnTiO{sub 6} (A=Pr, Gd): Rietveld refinement, and dielectric studies

Double perovskite related oxide A{sub 2}ZnTiO{sub 6}A=Pr, Gd were synthesized by the solid state reaction method at 1523 K. The structure and microstructure of the compounds were studied by X-ray, SAED and FESEM. Rietveld refinement of the powder X-ray analysis shows that the compounds crystallizes in monoclinic space group P2{sub 1}/n (a{sup +}b{sup −}b{sup −}) with unit cell parameter √2a{sub p}×√2a{sub p}×2a{sub p} (a=5.5026(1) Å, b=5.6305(1) Å, c=7.8149(1) Å, β=90.02(1)° for Pr{sub 2}ZnTiO{sub 6} and a=5.3621(1) Å, b=5.6565(2) Å, c=7.6779(2) Å and β=90.264(2)° for Gd{sub 2}ZnTiO{sub 6}. Electron diffraction study confirms P2{sub 1}/n symmetry of the oxides. The monoclinic distortion is larger in Gd{sub 2}ZnTiO{sub 6} than Pr{sub 2}ZnTiO{sub 6} which is associated with the tolerance factor and the tilting angle of ZnO{sub 6} and TiO{sub 6} octahedra (ϕ=13.64° for Pr{sub 2}ZnTiO{sub 6} and 16.51° for Gd{sub 2}ZnTiO{sub 6}). The compounds are highly ordered. The charge and size difference between B site cations are the driving force for the ordering of the B′O{sub 6} and B″O{sub 6} octahedra. Pr{sub 2}ZnTiO{sub 6} shows a dielectric constant of 27 and dielectric loss of 0.003 while Gd{sub 2}ZnTiO{sub 6} has a dielectric constant of 17 and dielectric loss of 0.005 measured at 1more » MHz. - Graphical abstract: Synthesis of new double perovskite dielectric material with very low dielectric loss. - Highlights: • Synthesis of new monoclinically distorted double perovskite (Pr{sub 2}ZnTiO{sub 6}). • Synthesis of monoclinically distorted double perovskite (Gd{sub 2}ZnTiO{sub 6}). • Selected area electron diffraction study of A{sub 2}ZnTiO{sub 6} (A=Pr, Gd). • Study of dielectric properties of A{sub 2}ZnTiO{sub 6} (A=Pr, Gd)« less
Authors:
; ;  [1] ;  [2] ;  [1]
  1. Department of Chemistry, Indian Institute of Technology, Delhi, Hauz Khas, New Delhi 110016 (India)
  2. Department of Chemistry, University of Delhi, New Delhi 110007 (India)
Publication Date:
OSTI Identifier:
22486755
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 229; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; DIELECTRIC MATERIALS; ELECTRON DIFFRACTION; GADOLINIUM COMPOUNDS; LATTICE PARAMETERS; MHZ RANGE; MICROSTRUCTURE; MONOCLINIC LATTICES; PERMITTIVITY; PEROVSKITE; POWDERS; PRASEODYMIUM COMPOUNDS; RELAXATION LOSSES; SYNTHESIS; TITANIUM OXIDES; ZINC COMPOUNDS; ZINC OXIDES