Title: Thermal stability of bimodal microstructure in magnesium alloy AZ91 processed by ECAP

The changes in microstructure of equal channel angular pressing (ECAP) processed magnesium alloy AZ91 during thermal exposure were studied in this paper. The microstructure stability was investigated by means of electron backscatter diffraction (EBSD), which allowed to measure the changes in grain size, mutual ratio of low-angle boundaries (LABs) to high-angle ones (HABs) and local lattice distortion evaluated by the kernel average misorientation (KAM) parameter. It was found experimentally that the threshold temperature at which significant grain coarsening takes place is 350 °C. No modification to mean grain diameter occurs below this temperature, nonetheless, some changes in LAB and HAB fraction, as well as in local lattice distortion, can be observed. - Highlights: • Thermal stability of bimodal UFG AZ91 alloy was assessed by means of EBSD. • Threshold temperature for pronounced grain coarsening was found at 350 °C. • Below 350 °C increase in LAB fraction and local lattice distortion takes place. • Local lattice distortion (LLD) can be well described using KAM approach. • LLD is influenced by coarsening and precipitation of Mg{sub 17}Al{sub 12} particles.
Authors:
 [1] ;  [2] ;  [1] ;  [2] ;  [1]
  1. Institute of Materials Science and Engineering, Faculty of Mechanical Engineering, Brno University of Technology, Technická 2896/2, 616 69 Brno (Czech Republic)
  2. (Czech Republic)
Publication Date:
OSTI Identifier:
22476165
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Characterization; Journal Volume: 107; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; BACKSCATTERING; ELECTRON DIFFRACTION; GRAIN SIZE; KERNELS; MAGNESIUM ALLOYS; MODIFICATIONS; PRECIPITATION; PRESSING; STABILITY