Title: Relationship between crystallographic structure of the Ti{sub 2}O{sub 3}/MnS complex inclusion and microstructure in the heat-affected zone (HAZ) in steel processed by oxide metallurgy route and impact toughness

A new method based on electron back scattered diffraction (EBSD) is proposed to determine the structure of titanium oxide/MnS complex inclusion which induced the formation of intragranular acicular ferrite (IAF) in heat-affected zone (HAZ) in steel processed by oxide metallurgy route. It was found that the complex inclusion was Ti{sub 2}O{sub 3}/MnS, the orientation relationship between Ti{sub 2}O{sub 3} and MnS was also examined, and the crystallographic orientation relationship among IAF, Ti{sub 2}O{sub 3}/MnS complex inclusion, austenite, bainite formed at lower temperature is researched systematically. It was observed that MnS precipitated on Ti{sub 2}O{sub 3} at specific habit plane and direction and MnS had a specific orientation relationship ((0001) Ti{sub 2}O{sub 3}//(111) MnS), <10–10> Ti{sub 2}O{sub 3}//<110> MnS) with respect to Ti{sub 2}O{sub 3}. Intragranular acicular ferrite (IAF) nucleated on MnS part of the Ti{sub 2}O{sub 3}/MnS complex inclusion had no specific orientation relationship with MnS. IAF and the surrounding bainite had different Bain groups, so that there was an increase in high angle boundaries, which was beneficial for the toughness of HAZ. - Highlights: • The inclusion of TiO{sub x}/MnS that induced IAF formation is identified to be Ti{sub 2}O{sub 3}/MnS. • The inclusion is identified based on electronmore » back scattered diffraction (EBSD). • MnS and Ti{sub 2}O{sub 3} had specific orientation relationship of Ti{sub 2}O{sub 3}/MnS complex inclusion. • The IAFs formed on the same inclusion tend to be in one Bain group. • IAF and the surrounding bainite tend to be in different Bain groups.« less
Authors:
;  [1] ;  [1] ;  [1] ;  [2]
  1. School of Materials Science and Engineering, University of Science and Technology Beijing (China)
  2. Laboratory for Excellence in Advanced Steel Research, Center for Structural and Functional Materials Research and Innovation, Department of Metallurgical and Materials Engineering, University of Texas at El Paso, 500 W. University Avenue, El Paso, TX 79968 (United States)
Publication Date:
OSTI Identifier:
22476137
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Characterization; Journal Volume: 106; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; AUSTENITE; BACKSCATTERING; BAINITE; CRYSTALLOGRAPHY; ELECTRON DIFFRACTION; HEAT AFFECTED ZONE; MANGANESE SULFIDES; METALLURGY; MICROSTRUCTURE; PRECIPITATION; TITANIUM OXIDES