Title: Sr{sub 1.98}Eu{sub 0.02}SiO{sub 4} luminescence whisker based on vapor-phase deposition: Facile synthesis, uniform morphology and enhanced luminescence properties

Highlights: • For the first time, it is possible to obtain Sr{sub 1.98}Eu{sub 0.02}SiO{sub 4} whisker. • The whiskers are smooth and uniform with L/D ratio over 50. • Durability and thermal stability of the whisker are enhanced. - Abstract: A high performance strontium silicate phosphor has been successfully synthesized though a facile vapor-phase deposition method. The product consists of single crystal whiskers which are smooth and uniform, and with a sectional equivalent diameter of around 5 μm; the aspect ratio is over 50 and no agglomeration can be observed. X-ray diffraction result confirmed that the crystal structure of the whisker was α’-Sr{sub 2}SiO{sub 4}. The exact chemical composition was Sr{sub 1.98}Eu{sub 0.02}SiO{sub 4} which was analyzed by energy dispersive spectrometer and inductively coupled plasma-mass spectrometer. The whisker shows broad green emission with peak at 523 nm ranging from 470 to 600 nm (excited at 370 nm). Compared with traditional Sr{sub 2}SiO{sub 4}:Eu phosphor, durability (at 85% humidity and 85 °C) and thermal stability of the whisker are obviously improved. Moreover, growth mechanism of the Sr{sub 1.98}Eu{sub 0.02}SiO{sub 4} whiskers is Vapor–Liquid–Solid. On a macro-scale, the product is still powder which makes it suitable for the current packaging process ofmore » WLEDs.« less
Authors:
 [1] ;  [1] ;  [2] ; ;  [1] ;  [3] ;  [3]
  1. Department of Materials Science and Engineering, Xiamen University, Xiamen 361005 (China)
  2. (Iraq)
  3. (China)
Publication Date:
OSTI Identifier:
22475995
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 71; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; AGGLOMERATION; CRYSTAL GROWTH; CRYSTAL STRUCTURE; DEPOSITION; EUROPIUM SILICATES; HARDNESS; LUMINESCENCE; MASS SPECTROMETERS; PERFORMANCE; PHOSPHORS; POWDERS; SOLIDS; STABILITY; STRONTIUM COMPOUNDS; STRONTIUM SILICATES; SYNTHESIS; TRANSMISSION ELECTRON MICROSCOPY; WEAR RESISTANCE; WHISKERS; X-RAY DIFFRACTION