Title: Up-conversion routines of Er{sup 3+}–Yb{sup 3+} doped Y{sub 6}O{sub 5}F{sub 8} and YOF phosphors

Highlights: • Single-phase optical materials of Y{sub 6}O{sub 5}F{sub 8}:Er and YOF:Er were prepared. • Effective spectral converting properties were observed in Y{sub 6}O{sub 5}F{sub 8}:Er,Yb. • 980 nm diode laser was irradiated for up-converting analysis. • A multi-photon process in the phosphors was investigated. - Abstract: Optical materials composed of a Y{sub 6(1−p−q)}Er{sub 6p}Yb{sub 6q}O{sub 5}F{sub 8} (p = 0.001–0.1, q = 0.005–0.1) solid solution with Y{sub 0.99}Er{sub 0.01}OF were prepared via a solid-state reaction using excess NH{sub 4}F flux at 950 °C for 30 min. X-ray diffraction patterns of Y{sub 6(1−p−q)}Er{sub 6p}Yb{sub 6q}O{sub 5}F{sub 8} and Y{sub 0.99}Er{sub 0.01}OF were compared upon altering the synthesis temperature and the molar ratio of the NH{sub 4}F flux to the Y{sup 3+} (Er{sup 3+}, Yb{sup 3+}) ions. The effective spectral-conversion properties of Er{sup 3+} and Er{sup 3+}–Yb{sup 3+} ions in Y{sub 6}O{sub 5}F{sub 8} phosphors were monitored during excitation with a 980 nm wavelength diode-laser. Selection of appropriate Er{sup 3+} and/or Yb{sup 3+} concentrations in the Y{sub 6}O{sub 5}F{sub 8} structure led to achievement of the desired up-conversion emission, from the green to the red regions of the spectra. Furthermore, the mechanism of up-conversion in the phosphors was described by anmore » energy-level schematic. Up-conversion emission spectra and the dependence of the emission intensity on pump power (between 193 and 310 mW) in the Y{sub 6(0.995−q)}Er{sub 0.03}Yb{sub 6q}O{sub 5}F{sub 8} phosphors were also investigated.« less
Authors:
 [1] ; ; ; ;  [1] ; ; ;  [2]
  1. Center for Green Fusion Technology and Department of Engineering in Energy & Applied Chemistry, Silla University, Busan 617-736 (Korea, Republic of)
  2. Center for Materials Architecturing, Institute of Multidisciplinary Convergence of Materials, Korea Institute of Science and Technology, Seoul 130-650 (Korea, Republic of)
Publication Date:
OSTI Identifier:
22475987
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 71; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; AMMONIUM FLUORIDES; COMPARATIVE EVALUATIONS; CONVERSION; DOPED MATERIALS; EMISSION; EMISSION SPECTRA; ERBIUM ADDITIONS; EXCITATION; LASER RADIATION; MULTI-PHOTON PROCESSES; OXYFLUORIDES; PHOSPHORS; SOLID SOLUTIONS; SYNTHESIS; X-RAY DIFFRACTION; YTTERBIUM ADDITIONS; YTTRIUM COMPOUNDS