Title: Hydrothermal synthesis of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanotubes for enhanced photoluminescence properties

Highlights: • Eu{sup 3+} doped Y{sub 2}O{sub 3} nanotubes. • Hydrothermal synthesis of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanostructures assissted with a further heat treatment. • Tunable coating ratios of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanophosphor. • Enhanced photoluminescence intensity of Y{sub 2}O{sub 3}:Eu{sup 3+} more than 60% by Y{sub 2}O{sub 3} surface coating. - Abstract: Novel Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanotubes with different coating ratios were synthesized successfully by a facile two-step process, including hydrothermal synthesis of Y(OH){sub 3} coated Y(OH){sub 3}:Eu{sup 3+} as precursors and then calcination of them at 1000 °C for 2 h. X-ray diffraction patterns and field emission scanning electron microscope images indicated these Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} phosphors possess tubular nanostructures. The photoluminescence properties of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} were systematically investigated by photoluminescence spectra, and photoluminescence enhancement was observed after proper coating. In other words, the coating ratio played a crucial role in photoluminescence efficiency. When it was 1/9, the photoluminescence intensity of {sup 5}D{sub 0} → {sup 7}F{sub 2} emission (about 613 nm) was 60% higher than that of Y{sub 2}O{sub 3}: Eu{sup 3+}more » phosphors under 255 nm excitation. Therefore, surface coating may be an alternative route for enhanced photoluminescence properties of the Y{sub 2}O{sub 3}:Eu{sup 3+} red-emitting phosphor.« less
Authors:
 [1] ;  [2] ; ; ;  [1]
  1. Department of Materials Forming and Control Engineering, Faculty of Mechanical Engineering & Automation, Zhejiang Sci-Tech University, Hangzhou 310018 (China)
  2. College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018 (China)
Publication Date:
OSTI Identifier:
22475973
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
77 NANOSCIENCE AND NANOTECHNOLOGY; DOPED MATERIALS; EFFICIENCY; EUROPIUM ADDITIONS; EXCITATION; FIELD EMISSION; HEAT TREATMENTS; HYDROTHERMAL SYNTHESIS; NANOTUBES; PHOSPHORS; PHOTOLUMINESCENCE; PRECURSOR; SCANNING ELECTRON MICROSCOPY; SPECTRA; SURFACE COATING; SURFACES; X-RAY DIFFRACTION; YTTRIUM HYDROXIDES; YTTRIUM OXIDES