Title: NaLa(MoO{sub 4}){sub 2}: RE{sup 3+} (RE{sup 3+} = Eu{sup 3+}, Sm{sup 3+}, Er{sup 3+}/Yb{sup 3+}) microspheres: the synthesis and optical properties

The strong green upconversion (UC) emission were observed in various Er{sup 3+}, Yb{sup 3+} co-doped NaLa(MoO{sub 4}){sub 2} samples synthesized via a hydrothermal route. The UC intensity depends on the dopant concentration, and the optimal UC emission was obtained in NaLa(MoO{sub 4}){sub 2}: 0.02Er{sup 3+}/0.10 Yb{sup 3+}. - Highlights: • The NaLa(MoO{sub 4}){sub 2} microspheres doped with Eu{sup 3+}, Sm{sup 3+} and Er{sup 3+}/Yb{sup 3+} were synthesized by a hydrothermal method. • The effects of the EDTA in the initial solution crystal phase and morphology were studied. • The down-conversion luminescence properties of NaLa(MoO{sub 4}){sub 2}: RE{sup 3+} (RE{sup 3+} = Eu{sup 3+}, Sm{sup 3+}) were investigated. • The UC luminescence properties and mechanism of Er{sup 3+}/Yb{sup 3+} co-doped NaLa(MoO{sub 4}){sub 2} was discussed. - Abstract: NaLa(MoO{sub 4}){sub 2}: RE{sup 3+} (RE{sup 3+} = Eu{sup 3+}, Sm{sup 3+}) microspheres have been synthesized at 180 °C via a facile EDTA-mediated hydrothermal route. X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), photoluminescence (PL) spectra were employed to characterize the samples. It was found that the amount of EDTA in the initial solution was responsible for crystal phase and shape determination. The effect of Eu{sup 3+} and Sm{sup 3+} doping concentrations on themore » luminescent intensity was also investigated in details. Furthermore, the up-conversion (UC) emissions have been observed in a series of Er{sup 3+}/Yb{sup 3+} co-doped NaLa(MoO{sub 4}){sub 2} samples. Concentration dependent studies revealed that the optimal composition was realized for a 2% Er{sup 3+} and 10% Yb{sup 3+}-doping concentration.« less
Authors:
 [1] ;  [2] ; ;  [1] ;  [1] ;  [3] ;  [4] ;  [5]
  1. Key Laboratory of Coherent Light, Atomic and Molecular Spectroscopy, Ministry of Education, College of Physics, Jilin University, Changchun 130023 (China)
  2. College of Chemistry and Biology, Beihua University, Jilin 132013 (China)
  3. (China)
  4. State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)
  5. Department of Physics, Pukyong National University, Busan 608-737 (Korea, Republic of)
Publication Date:
OSTI Identifier:
22475963
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; CONCENTRATION RATIO; CRYSTALS; DOPED MATERIALS; ERBIUM ADDITIONS; EUROPIUM ADDITIONS; FIELD EMISSION; HYDROTHERMAL SYNTHESIS; LANTHANUM COMPOUNDS; MICROSPHERES; MOLYBDATES; OPTICAL PROPERTIES; PHOTOLUMINESCENCE; SAMARIUM ADDITIONS; SCANNING ELECTRON MICROSCOPY; SODIUM COMPOUNDS; SPECTRA; X-RAY DIFFRACTION; YTTERBIUM ADDITIONS