Title: The structure, thermal expansion and phase transition properties of Ho{sub 2}Mo{sub 3−x}W{sub x}O{sub 12} (x = 0, 1.0, 2.0) solid solutions

Graphical abstract: A polymorph with Gd{sub 2}Mo{sub 3}O{sub 12}-type structure (space group: Pba2) for negative thermal expansion material Ho{sub 2}Mo{sub 3}O{sub 12} is observed above 700 °C, this polymorphism could be effectively supressed by W-substiution for Mo, the give the temperature dependence of Pba2 phase contents for Ho{sub 2}Mo{sub 3−x}W{sub x}O{sub 12} (x = 0.0, 1.0, 2.0). - Highlights: • The solid solution Ho{sub 2}Mo{sub 3−x}W{sub x}O{sub 12} was investigated by in situ X-ray diffraction. • It is found that the substitution slightly influence thermal expansion property. • A polymorph of Ho{sub 2}Mo{sub 3}O{sub 12} with Pba2 space group was observed above 700 °C. • The W-substitution for Mo effectively suppresses this transformation. - Abstract: Three solid solutions of Ho{sub 2}Mo{sub 3−x}W{sub x}O{sub 12}(x = 0, 1.0, 2.0) were prepared by solid state reaction method, the temperature dependent in-situ X-ray diffraction and thermal analysis were performed to investigate their structure and thermal expansion. All samples have orthorhombic structure(space group Pbcn# 60) with negative thermal expansion at the room temperature. the substitution of W for Mo enlarges the lattice constant and slightly influences the negative thermal expansion. An irreversible phase transformation to the Pba2 phase(Tb{sub 2}Mo{sub 3}O{sub 12} structure) was observedmore » at high temperature for Mo-rich samples. This ploymorphism could be effectively suppressed by the W-substitution for Mo, this phenomenon could be explained by the lower electronegativity of W{sup 6+} than Mo{sup 6+}.« less
Authors:
; ; ; ; ;
Publication Date:
OSTI Identifier:
22475950
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; CRYSTAL STRUCTURE; ELECTRONEGATIVITY; HOLMIUM COMPOUNDS; LATTICE PARAMETERS; MOLYBDENUM COMPOUNDS; ORTHORHOMBIC LATTICES; PHASE TRANSFORMATIONS; SOLID SOLUTIONS; SOLIDS; SPACE GROUPS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0273-0400 K; THERMAL ANALYSIS; THERMAL EXPANSION; TUNGSTATES; X-RAY DIFFRACTION