Title: Photoluminescence and cathodoluminescence properties of Eu{sup 3+} ions activated AMoO{sub 4} (A = Mg, Ca, Sr, Ba) phosphors

Highlights: • Under 393 nm excitation, strong red emission located at 615 nm was observed in all the samples. • The Eu{sup 3+}-activated CaMoO{sub 4} phosphor exhibited the strongest PL properties. • The CIE chromaticity coordinate of Eu{sup 3+}-activated CaMoO{sub 4} phosphor was (0.647,0.352). • The color purity of Eu{sup 3+}-activated CaMoO{sub 4} phosphor was 92.8%. • Strong CL properties were observed in the Eu{sup 3+}-activated CaMoO{sub 4} phosphor. - Abstract: Eu{sup 3+}-activated AMoO{sub 4} (A = Mg, Ca, Sr, Ba) phosphors were synthesized by a solid-state reaction method. Photoluminescence and cathodoluminescence (CL) spectra as well as X-ray diffraction patterns were measured to characterize the fabricated samples. Under 393 nm excitation, strong red emissions located at ∼615 nm corresponding to the {sup 5}D{sub 0} → {sup 7}F{sub 2} transition of Eu{sup 3+} ions were observed in all the samples. Compared with other Eu{sup 3+} ions activated AMoO{sub 4} (A = Mg, Sr, Ba) phosphors, Eu{sup 3+}-activated CaMoO{sub 4} phosphor exhibited the strongest red emission intensity with better Commission Internationale de L’Eclairage chromaticity coordinate and higher color purity. Furthermore, the CL results indicated that the Eu{sup 3+}-activated CaMoO{sub 4} phosphor had excellent luminescence properties.
Authors:
;
Publication Date:
OSTI Identifier:
22475941
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; BARIUM COMPOUNDS; CALCIUM COMPOUNDS; CATHODOLUMINESCENCE; COLOR; COMPARATIVE EVALUATIONS; EUROPIUM ADDITIONS; EXCITATION; IMPURITIES; MAGNESIUM COMPOUNDS; MOLYBDATES; PHOSPHORS; PHOTOLUMINESCENCE; SOLIDS; SPECTRA; STRONTIUM COMPOUNDS; X-RAY DIFFRACTION