Enhancement of persistent luminescence of ZnTa{sub 2}O{sub 6}:Pr{sup 3+} by addition Li{sup +}, Na{sup +}, K{sup +} and Cs{sup +} ions
Graphical abstract: The incorporation of the alkali metals (Li, Na, K and Cs) as co-dopants in ZnTa{sub 2}O{sub 6}:Pr{sup 3+} phosphor improved the lifetime of the persistent emission by increasing the quantity of the electron trapping centres. - Highlights: • ZnTa{sub 2}O{sub 6}:Pr{sup 3+} was co-doped with Li{sup +}, Na{sup +}, K{sup +} or Cs{sup +} ions. • Phase pure samples were synthesised. • Enhancement of the persistent emission was achieved by co-doping. • Corresponding electron trapping centres were quantified by a TL reader. - Abstract: Enhancement of the persistent emission was achieved by co-doping ZnTa{sub 2}O{sub 6}:Pr{sup 3+} with Li{sup +}, Na{sup +}, K{sup +} or Cs{sup +} ions. Phase pure samples were synthesised and it was confirmed by the X-ray diffraction pattern which matches that of the standard data. Incorporation of the co-dopant ions introduced strain into the phosphor, which increased with an increase in the ionic radius of the co-dopant ion. The scanning electron microscope image shows that the particles were agglomerated, and the surface images obtained using the Time of flight secondary ion mass spectroscopy showed that the dopant and the co-dopant ions in the phosphor were homogeneously distributed. The persistent emission was enhanced by the co-dopant ions as shown by the lifetime values calculated from the phosphorescence decay curves, and the corresponding electron trapping centres were quantified by thermoluminescence reader.
- OSTI ID:
- 22475940
- Journal Information:
- Materials Research Bulletin, Vol. 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Photoluminescence, thermally stimulated luminescence and electron paramagnetic resonance investigations of Tb{sup 3+} doped SrBPO{sub 5}
Near white light emitting ZnAl{sub 2}O{sub 4}:Dy{sup 3+} nanocrystals: Sol–gel synthesis and luminescence studies
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
CESIUM ADDITIONS
DEFECTS
DOPED MATERIALS
ION MICROPROBE ANALYSIS
LIFETIME
LITHIUM ADDITIONS
MASS SPECTROSCOPY
OPTICAL PROPERTIES
PHOSPHORESCENCE
PHOSPHORS
PHOTOELECTRON SPECTROSCOPY
POTASSIUM ADDITIONS
PRASEODYMIUM ADDITIONS
SCANNING ELECTRON MICROSCOPY
SODIUM ADDITIONS
SURFACES
SYNTHESIS
THERMOLUMINESCENCE
TIME-OF-FLIGHT METHOD
X-RAY DIFFRACTION