Title: Synthesis and electrochemical assessment of Ce{sub 0.5}Yb{sub 0.5}O{sub 1.75} ceramics and derived composite electrolytes

Highlights: • Ce{sub 0.5}Yb{sub 0.5}O{sub 1.75} prepared for the first time through solid state reaction. • High energy milling needed to assist the ceramic route. • Ce{sub 0.5}Yb{sub 0.5}O{sub 1.75} is oxide-ion conductor in air and n-type conductor at low pO{sub 2}. • Ce{sub 0.5}Yb{sub 0.5}O{sub 1.75} decomposes slightly when exposed to alkaline carbonates. • Composites based on Ce{sub 0.5}Yb{sub 0.5}O{sub 1.75} show standard electrical performance. - Abstract: Ce{sub 0.5}Yb{sub 0.5}O{sub 1.75} was prepared for the first time through high temperature (1600 °C for 5 h) solid state reaction, after high energy milling to enhance the mechano-chemical interaction of precursor oxides (CeO{sub 2} and Yb{sub 2}O{sub 3}). Single phase formation was confirmed by powder X-ray diffraction. Impedance spectroscopy data obtained under wide temperature (300–800 °C) and oxygen partial pressure (0.21 to about 10{sup −25} atm) ranges indicates that this material exhibits predominant oxide-ion conductivity under oxidizing conditions while n-type electronic conductivity prevails at low oxygen partial pressure. The mixed oxide shows modest ionic conductivity (1.1 × 10{sup −3} S cm{sup −1} at 800 °C) with activation energy of 1.3 eV in the 600–800 °C temperature range. When combined with molten carbonates (Li{sub 2}CO{sub 3} + Na{sub 2}CO{sub 3}, 1:1 molarmore » ratio) to produce composite electrolytes, Ce{sub 0.5}Yb{sub 0.5}O{sub 1.75} slightly decomposed. However, the composite electrical performance is still acceptable and closely matches the conductivity of similar materials (>0.1 S cm{sup −1} immediately above 500 °C)« less
Authors:
; ;
Publication Date:
OSTI Identifier:
22475931
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ACTIVATION ENERGY; CERAMICS; CERIUM OXIDES; ELECTROCHEMISTRY; ELECTROLYTES; IONIC CONDUCTIVITY; MILLING; N-TYPE CONDUCTORS; PARTIAL PRESSURE; PERFORMANCE; POWDERS; PRECURSOR; SOLIDS; SPECTROSCOPY; SYNTHESIS; X-RAY DIFFRACTION; YTTERBIUM OXIDES