Title: Luminescence properties of ZrW{sub 2}O{sub 8}:Eu{sup 3+} nanophosphors for white light emitting diodes

Highlights: • Eu{sup 3+} ions occupy C{sub 1} point group of the Zr{sup 4+} site in ZrW{sub 2}O{sub 8} crystals. • The optimum doping concentration of Eu{sup 3+} was determined for the red emission. • ZrW{sub 2}O{sub 8}:Eu possess high quantum efficiency and suitable chromaticity coordinates. - Abstract: ZrW{sub 2}O{sub 8}:Eu{sup 3+} nanophosphors (ca. 60 nm) with different Eu{sup 3+} doping concentrations were obtained using hydrothermal syntheses. X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), photoluminescence excitation and emission spectra as well as decay curve measurements were used for the characterization. Under 466 nm excitation, strong red emission at 616 nm corresponding to {sup 5}D{sub 0}–{sup 7}F{sub 2} transition of Eu{sup 3+} was observed for ZrW{sub 2}O{sub 8}:Eu{sup 3+} (9 mol%) phosphors. The values of intensity parameter Ω{sub 2} and Ω{sub 4} are 17.82 × 10{sup −20} cm{sup 2} and 1.092 × 10{sup −20} cm{sup 2}, respectively. The high quantum efficiency of 83.5% of the ZrW{sub 2}O{sub 8}:Eu{sup 3+} (9 mol%) suggests this material could be promising red phosphor for generating white light in phosphor-converted white light-emitting diodes (LED)
Authors:
; ; ; ;
Publication Date:
OSTI Identifier:
22475882
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 70; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
77 NANOSCIENCE AND NANOTECHNOLOGY; CRYSTALS; EMISSION SPECTRA; EUROPIUM ADDITIONS; HYDROTHERMAL SYNTHESIS; LIGHT EMITTING DIODES; PHOSPHORS; PHOTOLUMINESCENCE; QUANTUM EFFICIENCY; SCANNING ELECTRON MICROSCOPY; TRANSMISSION ELECTRON MICROSCOPY; VISIBLE RADIATION; X-RAY DIFFRACTION; ZIRCONIUM TUNGSTATES