Title: Synthesis of TiO{sub 2} nanoparticles by self-assembling reverse micelle cores of PS-b-PAA for functional textile applications

Highlights: • TiO{sub 2} nanoparticles were synthesized within poly(styrene)-b-poly(acrylic acid) micelles. • The copolymer solution including nano TiO{sub 2} was coated onto textile fabrics. • UV-protective factor of nano TiO{sub 2} coated fabrics was estimated as 50+. • Nano TiO{sub 2} coated fabrics was found to exhibit a high photocatalytic activity. - Abstract: Titanium dioxide (i.e., titanium(IV) oxide, TiO{sub 2}) nanoparticles have been fabricated using a copolymer templating technique in micellar solution of poly(styrene)-block-poly(acrylic acid), PS(10912)-b-PAA(4842) synthesized by atom transfer radical polymerization (ATRP). The size and morphology of the synthesized TiO{sub 2} nanoparticles have been characterized via TEM and XRD measurements. The average size of TiO{sub 2} nanoparticles was determined as 13 ± 3 and 13 ± 4 nm for titanium:copolymer ratios of 20:1 and 33:1, respectively. The copolymer solution including nano TiO{sub 2} particles has been coated onto textile fabrics to enhance their UV-blocking and self-cleaning properties. It has been determined that nano TiO{sub 2} coated textile fabrics have very good UV-blocking properties with 50+ of the ultraviolet protecting factor (UPF) and high photocatalytic efficiency with 69.2% of the photodegradation of methylene blue.
Authors:
; ; ;
Publication Date:
OSTI Identifier:
22475723
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 64; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
77 NANOSCIENCE AND NANOTECHNOLOGY; COPOLYMERS; NANOPARTICLES; NANOSTRUCTURES; PHOTOCATALYSIS; POLYMERIZATION; SYNTHESIS; TEXTILES; TITANIUM OXIDES; TRANSMISSION ELECTRON MICROSCOPY; ULTRAVIOLET RADIATION; X-RAY DIFFRACTION