Synthesis, crystal structure, thermal analysis and dielectric properties of [(C{sub 4}H{sub 9}){sub 4}N]{sub 3}Bi{sub 2}Cl{sub 9} compound
A new organic–inorganic tri-tetrabutylammonium nonachlorobibismuthate(III) compound was prepared. It was found to crystallize in the monoclinic system (P2{sub 1}/n space group) with the following lattice parameters: a=11.32(2) Å, b=22.30(3) Å, c=28.53(2) Å and β=96.52(0)°. The [Bi{sub 2}Cl{sub 9}]{sup 3−} anions are surrounded by six [(C{sub 4}H{sub 9})N]{sup +} cations, forming an octahedral configuration. These octahedra are sharing corners in order to provide the tri-dimensional network cohesion. The differential scanning calorimetry reveals four order-disorder reversible phase transitions located at 214, 238, 434 and 477 K. The Raman and infrared spectra confirm the presence of both cationic [(C{sub 4}H{sub 9})N]{sup +} and anionic [Bi{sub 2}Cl{sub 9}]{sup 3−} parts. The dielectric parameters, real and imaginary dielectric permittivity (ε′ and ε″), and dielectric loss tangent (tg δ), were measured in the frequency range of 209 kHz–5 MHz at different temperatures. The variations of dielectric dispersion (ε') and dielectric absorption (ε″) with frequency show a distribution of relaxation times, which is probably related to the change in the dynamical state of the [(C{sub 4}H{sub 9}){sub 4}N]{sup +} cations and the [Bi{sub 2}Cl{sub 9}]{sup 3−} anions. - Graphical abstract: Projection of the atomic arrangement of the [(C{sub 4}H{sub 9}){sub 4}N]{sub 3}Bi{sub 2}Cl{sub 9} compound along the b axis. - Highlights: • The structure of the (TBA){sub 3}Bi{sub 2}Cl{sub 9} compound was solved and reported. • The cristal belongs to the monoclinic system with P2{sub 1}/n space group. • DSC discloses four order–disorder reversible phases transitions. • The temperature-dependent permittivity ε' and ε″ has been investigated.
- OSTI ID:
- 22475675
- Journal Information:
- Journal of Solid State Chemistry, Vol. 227; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Unprecedented solid-state chemical reaction-from (C{sub 3}N{sub 2}H{sub 5}){sub 3}SbBr{sub 6}.H{sub 2}Oto(C{sub 3}N{sub 2}H{sub 5}){sub 5}Sb{sub 2}Br{sub 11}. From centrosymmetric to non-centrosymmetric crystal structure
The new silver(I)thioantimonate(III) [C{sub 4}N{sub 2}H{sub 14}][Ag{sub 3}Sb{sub 3}S{sub 7}] and a new structural variant of the silver(I)thioantimonate(III) [C{sub 2}N{sub 2}H{sub 9}]{sub 2}[Ag{sub 5}Sb{sub 3}S{sub 8}] both synthesized under solvothermal conditions
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ANIONS
BISMUTH CHLORIDES
CALORIMETRY
CATIONS
DIELECTRIC MATERIALS
INFRARED SPECTRA
KHZ RANGE
LATTICE PARAMETERS
MHZ RANGE
MONOCLINIC LATTICES
PERMITTIVITY
PHASE TRANSFORMATIONS
RAMAN SPECTRA
RAMAN SPECTROSCOPY
SYNTHESIS
TEMPERATURE DEPENDENCE
THERMAL ANALYSIS