Title: Synthetic and spectroscopic studies of vanadate glaserites I: Upconversion studies of doubly co-doped (Er, Tm, or Ho):Yb:K{sub 3}Y(VO{sub 4}){sub 2}

The synthesis and upconversion properties of trigonal glaserite-type K{sub 3}Y(VO{sub 4}){sub 2} co-doped with Er{sup 3+}/Yb{sup 3+}, Ho{sup 3+}/Yb{sup 3+}, or Tm{sup 3+}/Yb{sup 3+} were studied. Powder samples were synthesized by solid state reactions at 1000 °C for 48 h, while well-formed hexagonal single crystals of the same were grown hydrothermally using 10 M K{sub 2}CO{sub 3} at 560–650 °C. Infrared-to-visible upconversion by Er{sup 3+}/Yb{sup 3+}, Ho{sup 3+}/Yb{sup 3+}, or Tm{sup 3+}/Yb{sup 3+} codoped-K{sub 3}Y(VO{sub 4}){sub 2} glaserite powder and single crystals was observed, and the upconversion spectral properties were studied as a function of different Er{sup 3+}, Tm{sup 3+}, Ho{sup 3+}, and Yb{sup 3+} ion concentrations. The process is observed under 980 nm laser diode excitation and leads to strong green (552 nm) and red (659 nm) emission for Er{sup 3+}/Yb{sup 3+}, green (549 nm) and red (664 nm) emission for Ho{sup 3+}/Yb{sup 3+}, and blue (475 nm) and red (647 nm) emission for Tm{sup 3+}/Yb{sup 3+}. The main mechanism that allows for up-conversion is attributed the energy transfer among Yb{sup 3+} and the various Er{sup 3+}/Ho{sup 3+}/Tm{sup 3+} ions in excited states. These results illustrate the large potential of co-doped alkali double vanadates for photonic applications involving optoelectronicsmore » devices. - Graphical abstract: Synthesis and upconversion in vanadate glaserites. - Highlights: • K{sub 3}Y(VO{sub 4}){sub 2} codoped with Er, Tm, or Ho:Yb were synthesized via solid-state and hydrothermal routes. • Upconversion properties are investigated. • The codoped compounds revealed efficient infrared-to-visible upconversion. • The presented compounds are potential host for solid state lighting.« less
Authors:
; ; ; ;
Publication Date:
OSTI Identifier:
22475669
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 226; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; CONCENTRATION RATIO; CRYSTAL GROWTH; DOPED MATERIALS; ENERGY TRANSFER; ERBIUM COMPOUNDS; ERBIUM IONS; EXCITED STATES; HOLMIUM IONS; MONOCRYSTALS; OPTOELECTRONIC DEVICES; POTASSIUM CARBONATES; POWDERS; SOLIDS; SYNTHESIS; TEMPERATURE DEPENDENCE; THULIUM IONS; VANADATES; YTTERBIUM IONS; YTTRIUM COMPOUNDS