Crystal structure and ion conductivity of a new mixed-anion phosphate LiMg{sub 3}(PO{sub 4})P{sub 2}O{sub 7}
- Department of Chemistry, Division of Energy Systems Research, Ajou University, Suwon 443-749 (Korea, Republic of)
- Department of Chemistry, Yeungnam University, Gyeongsan 712-749 (Korea, Republic of)
A new lithium-containing phosphate, LiMg{sub 3}(PO{sub 4})P{sub 2}O{sub 7}, was prepared by a solid-state reaction, and it was characterized by an ab initio structure determination method on the basis of synchrotron powder X-ray diffraction data. LiMg{sub 3}(PO{sub 4})P{sub 2}O{sub 7} was found to be orthorhombic (space group Pnma) with lattice parameters a=9.0387(1) Å, b=10.6072(1) Å, c=8.3065(1) Å, and V=796.39(1) Å{sup 3}. The structure features infinite [Mg{sub 3}O{sub 10}]{sub ∞} layers that are parallel to the bc plane and that are interconnected along the a axis by PO{sub 4} and P{sub 2}O{sub 7} groups. The [Mg{sub 3}O{sub 10}]{sub ∞} layer contains Mg{sub 3}O{sub 14} trimers that are formed by three edge-shared MgO{sub 6} octahedra. The PO{sub 4} and P{sub 2}O{sub 7} groups are located alternatively between [Mg{sub 3}O{sub 10}]{sub ∞} layers. This gives rise to a three-dimensional framework that contains large tunnels along the directions [1 0 0] and [0 1 0]; the Li{sup +} ions are stabilized in these tunnels. AC impedance spectroscopy shows that LiMg{sub 3}(PO{sub 4})P{sub 2}O{sub 7} has an ionic conductivity of 3.40×10{sup −5} S cm{sup −1} at 769 K, with an activation energy of 1.17 eV. - Graphical abstract: Polyhedral view of LiMg3(PO4)P2O7. Li+ ions are represented by orange spheres, MgO6 groups by octahedra, and PO4 groups by tetrahedra. - Highlights: • New compound LiMg{sub 3}(PO{sub 4})P{sub 2}O{sub 7} is reported. • The crystal structure is investigated by synchrotron XRD analysis. • The structure features [Mg{sub 3}O{sub 10}]{sub ∞} layers with interconnecting PO{sub 4} and P{sub 2}O{sub 7} groups. • Correlation between the crystal structure and ionic conductivity is discussed.
- OSTI ID:
- 22475613
- Journal Information:
- Journal of Solid State Chemistry, Vol. 225; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystal structures and electronic properties for the over-lithiated and Li–Ag substituted phases of Li{sub 9}V{sub 3}(P{sub 2}O{sub 7}){sub 3}(PO{sub 4}){sub 2} insertion electrode system
Cathode of LiMg{sub y}Mn{sub 2{minus}y}O{sub 4} and LiMg{sub y}Mn{sub 2{minus}y}O{sub 4{minus}{delta}} spinel phases for lithium secondary batteries