Title: Nanostructured crystals of fluorite phases Sr{sub 1−x}R{sub x}F{sub 2+x} (R Are Rare Earth Elements) and their ordering: 10. Ordering under spontaneous crystallization and annealing of Sr{sub 1−x}R{sub x}F{sub 2+x} Alloys (R = Tb-Lu, Y) with 23.8–36.1 mol % RF{sub 3}

The products of spontaneous crystallization (at a cooling rate of ∼200 K/min) of Sr{sub 1−x}R{sub x}F{sub 2+x} melts in the homogeneity range of the fluorite phase have been investigated. Thirty-two irrational compositions with 23.8–36.1 mol % RF{sub 3} and eight rational Sr{sub 2}RF{sub 7} compositions are obtained. With respect to the RF{sub 3} content, these compositions form five groups: (1) Sr{sub 0.762}R{sub 0.238}F{sub 2.238} (23.8% RF{sub 3}), (2) Sr{sub 0.744}R{sub 0.256}F{sub 2.256} (25.6%), (3) Sr{sub 0.718}R{sub 0.282}F{sub 2.282} (28.2%), (4) Sr{sub 2}RF{sub 7} (33.3%), and (5) Sr{sub 0.639}R{sub 0.361}F{sub 2.361} (36.1%). R = Tb-Lu, Y for all groups. Quenching melts of group 5 with R = Tb, Dy, and Ho leads to the formation of ordered phases with the trigonal distortion of the rhβ-Na{sub 7}Zr{sub 6}F{sub 31} type, while for melts of group 5 with R = Lu, quenching yields a phase of the trigonal rhα′-Sr{sub 4}Lu{sub 3}F{sub 17} type. In group 5 with R = Y, Er, Tm, or Yb and in groups 1–4 with all REEs, fluorite phases are formed. Annealing at 900 ± 20°C for 96 h with subsequent cooling at a rate of ∼200 K/min expands the variety of ordered phases: a phase with a newmore » r type of orthorhombic distortion is formed in group 1 with R = Lu, in group 2 with R = Tm or Lu, and in group 3 with R = Ho-Lu, Y; a t-Sr{sub 2}RF{sub 7} phase with tetragonal distortion is formed in group 4 with R = Tb-Er, Y; and a phase of trigonal rhα′ type is formed in group 5 with R = Y, Yb, or Lu. A fluorite phase arises in group 1 with R = Tb-Lu, Y as a result of quenching and annealing. The tendency to ordering becomes more pronounced with an increase in the RF{sub 3} content and REE atomic number. The annealing conditions do not provide equilibrium or the completely ordered state of all alloys.« less
Authors:
; ; ; ; ;  [1]
  1. Russian Academy of Sciences, Shubnikov Institute of Crystallography (Russian Federation)
Publication Date:
OSTI Identifier:
22472486
Resource Type:
Journal Article
Resource Relation:
Journal Name: Crystallography Reports; Journal Volume: 60; Journal Issue: 1; Other Information: Copyright (c) 2015 Pleiades Publishing, Inc.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ANNEALING; COOLING; CRYSTALLIZATION; CRYSTALS; FLUORITE; LUTETIUM FLUORIDES; NANOSTRUCTURES; ORTHORHOMBIC LATTICES; QUENCHING; STRONTIUM COMPOUNDS; TERBIUM FLUORIDES; TETRAGONAL LATTICES; YTTRIUM FLUORIDES