Title: Ionic conductivity of binary fluorides of potassium and rare earth elements

The ionic conductivity s of KYF{sub 4} and K{sub 2}RF{sub 5} single crystals (R = Gd, Ho, Er) and KNdF{sub 4} and K{sub 2}RF{sub 5} ceramic samples (R = Dy, Er) has been studied in the temperature range of 340–500°C. A comparative analysis of the σ values for these objects has been performed. Binary fluorides of potassium and rare earth elements were synthesized by the hydrothermal method (temperature 480°C, pressure 100–150 MPa) in the R{sub 2}O{sub 3}–KF–H{sub 2}O systems. The σ values of tetraf luorides are 3 × 10{sup –5} S/cm (KYF{sub 4} single crystal) and 3 × 10{sup –6} S/cm (KNdF{sub 4} ceramics) at 435°C. A K{sub 2}ErF{sub 5} single crystal with σ = 1.2 × 10{sup –4} S/cm at 435°C has the maximum value of ionic conductivity among pentafluorides. The anisotropy of ionic transport was found in K{sub 2}HoF{sub 5} single crystals, σ{sub ∥c}/σ{sub ⊥c} = 2.5, where σ{sub ∥c} and σ{sub ⊥c} are, respectively, the conductivities along the crystallographic c axis and in the perpendicular direction.
Authors:
 [1]
  1. Russian Academy of Sciences, Shubnikov Institute of Crystallography (Russian Federation)
Publication Date:
OSTI Identifier:
22471924
Resource Type:
Journal Article
Resource Relation:
Journal Name: Crystallography Reports; Journal Volume: 61; Journal Issue: 1; Other Information: Copyright (c) 2016 Pleiades Publishing, Inc.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ANISOTROPY; CERAMICS; ERBIUM FLUORIDES; GADOLINIUM FLUORIDES; HOLMIUM FLUORIDES; HYDROTHERMAL SYNTHESIS; IONIC CONDUCTIVITY; MONOCRYSTALS; NEODYMIUM FLUORIDES; POTASSIUM FLUORIDES; TEMPERATURE DEPENDENCE; YTTRIUM FLUORIDES