Title: A novel process for recycling and resynthesizing LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} from the cathode scraps intended for lithium-ion batteries

Highlights: • A simple process to recycle cathode scraps intended for lithium-ion batteries. • Complete separation of the cathode material from the aluminum foil is achieved. • The recovered aluminum foil is highly pure. • LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} is directly resynthesized from the separated cathode material. - Abstract: To solve the recycling challenge for aqueous binder based lithium-ion batteries (LIBs), a novel process for recycling and resynthesizing LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} from the cathode scraps generated during manufacturing process is proposed in this study. Trifluoroacetic acid (TFA) is employed to separate the cathode material from the aluminum foil. The effects of TFA concentration, liquid/solid (L/S) ratio, reaction temperature and time on the separation efficiencies of the cathode material and aluminum foil are investigated systematically. The cathode material can be separated completely under the optimal experimental condition of 15 vol.% TFA solution, L/S ratio of 8.0 mL g{sup −1}, reacting at 40 °C for 180 min along with appropriate agitation. LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} is successfully resynthesized from the separated cathode material by solid state reaction method. Several kinds of characterizations are performed to verify the typical properties of the resynthesized LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} powder.more » Electrochemical tests show that the initial charge and discharge capacities of the resynthesized LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} are 201 mAh g{sup −1} and 155.4 mAh g{sup −1} (2.8–4.5 V, 0.1 C), respectively. The discharge capacity remains at 129 mAh g{sup −1} even after 30 cycles with a capacity retention ratio of 83.01%.« less
Authors:
 [1] ;  [2] ;  [2] ;  [2] ;  [1] ;  [2] ;  [2] ;  [1] ;  [2] ;  [2] ;  [1] ;  [2] ;  [2] ;  [2] ;  [1] ;  [2] ;  [2]
  1. National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology, Beijing 100190 (China)
  2. (China)
Publication Date:
OSTI Identifier:
22443595
Resource Type:
Journal Article
Resource Relation:
Journal Name: Waste Management; Journal Volume: 34; Journal Issue: 9; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; 12 MANAGEMENT OF RADIOACTIVE WASTES, AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES; ALUMINIUM; CATHODES; ELECTROCHEMISTRY; FOILS; LIQUIDS; LITHIUM ION BATTERIES; RECYCLING; SCRAP; SOLIDS