Title: Phase equilibria in the La–Mg–Ge system at 500 °C and crystal structure of the new ternary compounds La{sub 11}Mg{sub 2}Ge{sub 7} and LaMg{sub 3−x}Ge{sub 2}

The whole 500 °C isothermal section of the La–Mg–Ge ternary system was constructed. The existence and crystal structure of three ternary compounds were confirmed: La{sub 2+x}Mg{sub 1−x}Ge{sub 2} (τ{sub 2}, P4/mbm, tP10–Mo{sub 2}FeB{sub 2}, 0≤x≤0.25), La{sub 4}Mg{sub 5}Ge{sub 6} (τ{sub 3}, Cmc2{sub 1}, oS60–Gd{sub 4}Zn{sub 5}Ge{sub 6}) and La{sub 4}Mg{sub 7}Ge{sub 6} (τ{sub 4}, C2/m, mS34, own structure type). Five novel compounds were identified and structurally characterized: La{sub 11}Mg{sub 2}Ge{sub 7} (τ{sub 1}, P4{sub 2}/ncm, tP88-8, own structure type, a=1.21338(5), c=1.57802(6) nm), LaMg{sub 3−x}Ge{sub 2} (τ{sub 5}, P3{sup ¯}1c, hP34-0.44, own structure type, x=0.407(5), a=0.78408(4), c=1.45257(7) nm), La{sub 6}Mg{sub 23}Ge (τ{sub 6}, Fm3{sup ¯}m, cF120–Zr{sub 6}Zn{sub 23}Si, a=1.46694(6) nm), La{sub 4}MgGe{sub 10−x} (τ{sub 7}, x=0.37(1), C2/m, mS60-1.46, own structure type, a=0.88403(8), b=0.86756(8), c=1.7709(2) nm, β=97.16°(1) and La{sub 2}MgGe{sub 6} (τ{sub 8}, Cmce, oS72–Ce{sub 2}(Ga{sub 0.1}Ge{sub 0.9}){sub 7}, a=0.8989(2), b=0.8517(2), c=2.1064(3) nm). Disordering phenomena were revealed in several La–Mg–Ge phases in terms of partially occupied sites. The crystal structures of La{sub 11}Mg{sub 2}Ge{sub 7} and LaMg{sub 3−x}Ge{sub 2} are discussed in details. The latter is a √3a×√3a×2c superstructure of the LaLi{sub 3}Sb{sub 2} structure type; the symmetry reduction scheme is shown in the Bärnighausen formalism terms. - Graphical abstract: La–Mg–Ge isothermalmore » section at 500 °C and group–subgroup relation between the LaLi{sub 3}Sb{sub 2} (parent type) and LaMg{sub 3−x}Ge{sub 2} (derivative) structures. - Highlights: • Novel La−Mg−Ge compounds structure determination from X-ray single crystal data. • Disordering phenomena as common features of the studied germanides. • Bärnighausen formalism as a useful tool for accurate structure determination. • Full isothermal section of the La–Mg–Ge ternary system at 500 °C.« less
Authors:
 [1] ; ;  [1] ;  [2] ;  [3] ;  [1]
  1. Università degli Studi di Genova, Dipartimento di Chimica e Chimica Industriale, via Dodecaneso 31, 16146 Genova (Italy)
  2. Università degli Studi di Milano, Dipartimento di Chimica, Via Golgi 19, 20133 Milano (Italy)
  3. (SCTMS), Samara State University, Samara 443011 (Russian Federation)
Publication Date:
OSTI Identifier:
22443428
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 218; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; CUBIC LATTICES; GERMANIDES; MONOCLINIC LATTICES; MONOCRYSTALS; ORTHORHOMBIC LATTICES; PHASE DIAGRAMS; TETRAGONAL LATTICES; X RADIATION; X-RAY DIFFRACTION