Title: Inert blanketing of a hydride bed using typical grade protium

This paper describes the impact of 500 ppm (0.05%) impurities in protium on the absorption rate of a 9.66 kg LaNi{sub 4.25}Al{sub 0.75} (LANA0.75) metal hydride bed. The presence of 500 ppm or less inerts (i.e. non-hydrogen isotopes) can significantly impact hydrogen bed absorption rates. The impact on reducing absorption rates is significantly greater than predicted assuming uniform temperature, pressure, and compositions throughout the bed. Possible explanations are discussed. One possibility considered was the feed gas contained impurity levels higher than 500 ppm. It was shown that a level of 5000 ppm of inerts would have been necessary to fit the experimental result so this possibility wa dismissed. Another possibility is that the impurities in the protium supply reacted with the hydride material and partially poisoned the hydride. If the hydride were poisoned with CO or another impurity, the removal of the over-pressure gas in the bed would not be expected to allow the hydride loading of the bed to continue as the experimental results showed, so this possibility was also dismissed. The last possibility questions the validity of the calculations. It is assumed in all the calculations that the gas phase composition, temperature, and pressure are uniform throughout themore » bed. These assumptions are less valid for large beds where there can be large temperature, pressure, and composition gradients throughout the bed. Eventually the impact of 0.05% inerts in protium on bed absorption rate is shown and explained in terms of an increase in inert partial pressure as the bed was loaded.« less
Authors:
 [1]
  1. Savannah River National Laboratory, Aiken (United States)
Publication Date:
OSTI Identifier:
22429730
Resource Type:
Journal Article
Resource Relation:
Journal Name: Fusion Science and Technology; Journal Volume: 67; Journal Issue: 2; Conference: TRITIUM 2013: 10. International Conference on Tritium Science and Technology, Nice Acropolis (France), 21-25 Oct 2013; Other Information: Country of input: France; 8 refs.
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ABSORPTION; ALUMINIUM ALLOYS; CARBON MONOXIDE; HYDRIDES; HYDROGEN 1; IMPURITIES; LANTHANUM ALLOYS; NICKEL ALLOYS