Title: The fabrication of foam-like 3D mesoporous NiO-Ni as anode for high performance Li-ion batteries

Graphical abstract: Foam-like 3 dimensional (3D) mesoporous NiO on 3D micro-porous Ni was fabricated. - Highlights: • We prepare NiO-Ni foam composite via hydrothermal etching and subsequent annealing. • The NiO exhibits novel foam-like 3D mesoporous architecture. • The NiO-Ni anode shows good cycle stability. - Abstract: Foam-like three dimensional mesoporous NiO on Ni foam was fabricated via facile hydrothermal etching and subsequent annealing treatment. The porous NiO consists of a large number of nanosheets with mean thickness about 50 nm, among which a large number of mesoscopic pores with size ranges from 100 nm to 1 μm distribute. The electrochemical performance of the as-prepared NiO-Ni as anode for lithium ion battery was studied by conventional charge/discharge test, which shows excellent cycle stability and rate capability. It exhibits initial discharge and charge capacities of 979 and 707 mA h g{sup −1} at a charge/discharge rate of 0.7 C, which maintain of 747 and 738 mA h g{sup −1} after 100 cycles. Even after 60 cycles at various rates from 0.06 to 14 C, the 10th discharge and charge capacities of the NiO-Ni electrode can revert to 699 and 683 mA h g{sup −1} when lowering the charge/discharge rate to 0.06more » C.« less
Authors:
 [1] ;  [2] ; ; ; ; ;  [1] ;  [2]
  1. Key Laboratory Magnetism and Magnetic Material of Education Lanzhou University, Lanzhou 730000 (China)
  2. (China)
Publication Date:
OSTI Identifier:
22420845
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 63; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ANNEALING; ANODES; ELECTROCHEMISTRY; ETCHING; FABRICATION; FOAMS; LITHIUM ION BATTERIES; LITHIUM IONS; NANOSTRUCTURES; NICKEL; NICKEL OXIDES; POROUS MATERIALS; THREE-DIMENSIONAL LATTICES