Enhanced ferromagnetic properties and high temperature dielectric anomalies in Bi{sub 0.9}Ca{sub 0.05}Sm{sub 0.05}FeO{sub 3} prepared by hydrothermal method
- Department of Physics, Indian Institute of Technology Madras, Chennai 600036 (India)
- Department of Materials Science and Engineering, Seoul National University, Seoul 151-744 (Korea, Republic of)
- School of Chemistry and Molecular Biosciences, The University of Queensland, Brisbane, QLD 4072 (Australia)
Graphical abstract: Temperature variation of dielectric constant of Bi{sub 0.9}Ca{sub 0.05}Sm{sub 0.05}FeO{sub 3} at various frequencies as a function of temperature indicating anomalies at 420 and 540 K. - Highlights: • Substitution of Sm ions for Bi enhances the saturation magnetization of BiFeO{sub 3}. • XPS studies indicate the creation of oxygen vacancies upon Ca substitution. • Dielectric measurements show dielectric anomalies at high temperatures. • Raman spectra at high temperatures confirm the dielectric anomaly temperatures. - Abstract: Enhanced ferromagnetic properties and high temperature dielectric anomalies in the temperature range of 300–873 K in Bi{sub 0.9}Ca{sub 0.05}Sm{sub 0.05}FeO{sub 3} (BCSFO) prepared by hydrothermal method are reported. BiFeO{sub 3} is seen to crystallize in rhombohedrally distorted perovskite structure without any impurity phase. Substitution of small amount of Ca and Sm (Bi{sub 0.9}Ca{sub 0.05}Sm{sub 0.05}FeO{sub 3}) leads to increase in the lattice constant values and formation of small amount of secondary phase. Magnetization curve of pure BFO indicates very weak ferromagnetism combined with antiferromagnetic nature of the samples. Whereas, BCSFO sample shows very clear and enhanced ferromagnetic nature. Saturation magnetization and Neel’s temperature values are found to be 4.36 emu/g and 664 K, respectively. X-ray photoelectron spectroscopy indicates the creation of oxygen vacancies upon Ca substitution in Bi site. Dielectric anomalies at 420 and 540 K were observed for Bi{sub 0.9}Ca{sub 0.05}Sm{sub 0.05}FeO{sub 3} from the temperature variation of dielectric constant and specific heat capacity measurements. Observation of dielectric anomalies in pure BiFeO{sub 3} sample reveals that the origin of dielectric peaks is purely from the primary phase. Raman spectroscopy study indicates a clear shift and broadening of A modes (between 100 and 200 cm{sup −1}) at the dielectric anomaly temperatures supporting the observed dielectric anomalies.
- OSTI ID:
- 22420796
- Journal Information:
- Materials Research Bulletin, Vol. 62; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evidence of improved ferroelectric phase stabilization in Nd and Sc co-substituted BiFeO{sub 3}
Enhanced magnetization and improved insulating character in Eu substituted BiFeO{sub 3}
Related Subjects
ANTIFERROMAGNETISM
BISMUTH COMPOUNDS
CALCIUM COMPOUNDS
DIELECTRIC MATERIALS
FERRITES
FERROMAGNETISM
HYDROTHERMAL SYNTHESIS
LATTICE PARAMETERS
MAGNETIZATION
PERMITTIVITY
RAMAN SPECTRA
RAMAN SPECTROSCOPY
SAMARIUM COMPOUNDS
SAMARIUM IONS
SPECIFIC HEAT
TEMPERATURE DEPENDENCE
TRIGONAL LATTICES
VACANCIES
X-RAY PHOTOELECTRON SPECTROSCOPY