Title: The influence of a silica pillar in lamellar tetratitanate for selective catalytic reduction of NO{sub x} using NH{sub 3}

Highlights: • Potassium ions significantly affected the SCR. • The introduction of silica in the catalyst promotes the NH{sub 3}-SCR reaction. • The catalysts activities were not significantly influenced by SO{sub 2} addition. - Abstract: Silica-pillared layered titanate (SiO{sub 2}–Ti{sub 4}O{sub 9}) was prepared by intercalating organosilanes into the interlayers of a layered K{sub 2}Ti{sub 4}O{sub 9} followed by calcination at 500 °C. The lamellar titanates produced were used as a support to prepare vanadium catalysts (1 and 2 wt%) through wet impregnation for selective catalytic reduction (SCR) of NO. The catalysts were characterized using nitrogen adsorption (BET), X-ray diffraction (XRD), temperature programmed reduction (H{sub 2}-TPR), nuclear magnetic resonance ({sup 29}Si NMR), and infrared spectroscopy (FT-IR). Reduction of NO by NH{sub 3} was studied in a fixed-bed reactor packed with the catalysts and fed a mixture comprising 1% NH{sub 3}, 1% NO, 10% O{sub 2}, and 34 ppm SO{sub 2} (when used) in helium. The results demonstrate that activity is correlated with the support, i.e., with acidic strength of catalysts. The potassium in the support, K{sub 2}Ti{sub 4}O{sub 9}, significantly affected the reaction and level of vanadium species reduction. The catalyst (1VSiT) with 1 wt% vanadium impregnated on the SiO{submore » 2}–Ti{sub 4}O{sub 9} support reduced ∼80% of the NO. Approximately the same conversion rate was generated on the catalyst (2VSiT) with 2 wt% vanadium using the same support. The increased NH{sub 3} adsorption demonstrate that introduction of silica in the catalyst promotes the NH{sub 3}-SCR reaction. More importantly, 2VSiT and 1VSiT were strongly resistant to SO{sub 2} poisoning.« less
Authors:
; ;  [1] ;  [2] ;  [1]
  1. Institute of Chemistry, Federal University of Goiás, C. Postal 131, CEP 74001-970 Goiânia, GO (Brazil)
  2. Laboratory of Applied Catalysis, Department of Chemical Engineering, Federal University of Sao Carlos, Rodovia Washington Luis Km 235, C. Postal 676, CEP 13565-905 São Carlos, SP (Brazil)
Publication Date:
OSTI Identifier:
22420748
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 61; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ABSORPTION SPECTROSCOPY; ADSORPTION; AMMONIA; CALCINATION; CATALYSTS; FOURIER TRANSFORMATION; INFRARED SPECTRA; NITRIC OXIDE; NMR SPECTRA; NUCLEAR MAGNETIC RESONANCE; POTASSIUM COMPOUNDS; POTASSIUM IONS; SELECTIVE CATALYTIC REDUCTION; SILICA; SILICON 29; SILICON OXIDES; SULFUR DIOXIDE; TITANATES; VANADIUM; X-RAY DIFFRACTION