Synthesis, characterization, and catalytic application of ordered mesoporous carbon–niobium oxide composites

Journal Article · Sat Nov 15 00:00:00 EST 2014 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2014.07.007· OSTI ID:22420613

Gao, Juan-Li; Gao, Shuang; Liu, Chun-Ling; Liu, Zhao-Tie; Dong, Wen-Sheng

Graphical abstract: The ordered mesoporous carbon–niobium oxide composites have been synthesized by a multi-component co-assembly method associated with a carbonization process. - Highlights: • Ordered mesoporous carbon–niobium oxide composites were synthesized. • The content of Nb{sub 2}O{sub 5} in the composites could be tuned from 38 to 75%. • Niobium species were highly dispersed in amorphous carbon framework walls. • The composites exhibited good catalytic performance in the dehydration of fructose. - Abstract: Ordered mesoporous carbon–niobium oxide composites have been synthesized by a multi-component co-assembly method associated with a carbonization process using phenolic resol as carbon source, niobium chloride as precursor and amphiphilic triblock copolymer Pluronic F127 as template. The resulting materials were characterized using a combination of techniques including differential scanning calorimetry–thermogravimetric analysis, N{sub 2} physical adsorption, X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy. The results show that with increasing the content of Nb{sub 2}O{sub 5} from 38 to 75% the specific surface area decreases from 306.4 to 124.5 m{sup 2} g{sup −1}, while the ordered mesoporous structure is remained. Niobium species is well dispersed in the amorphous carbon framework. The mesoporous carbon–niobium oxide composites exhibit high catalytic activity in the dehydration of fructose to 5-hydroxymethylfurfural. A 100% conversion of fructose and a 76.5% selectivity of 5-hydroxymethylfurfural were obtained over the carbon–niobium oxide composite containing 75% Nb{sub 2}O{sub 5} under the investigated reaction conditions.

• OSTI ID: 22420613
• Journal Information: Materials Research Bulletin, Vol. 59; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ADSORPTION
CALORIMETRY
CARBON
CARBONIZATION
COMPOSITE MATERIALS
COPOLYMERS
DEHYDRATION
FRUCTOSE
NANOSTRUCTURES
NIOBIUM
NIOBIUM CHLORIDES
NIOBIUM OXIDES
PHENOLS
SPECIFIC SURFACE AREA
SYNTHESIS
THERMAL GRAVIMETRIC ANALYSIS
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
X-RAY PHOTOELECTRON SPECTROSCOPY