Title: Structural and magnetic properties of La–Co substituted Sr–Ca hexaferrites synthesized by the solid state reaction method

Graphical abstract: The change of the remanence (B{sub r}) and intrinsic coercivity (H{sub cj}) with La content (x) and Co content (y) of hexagonal ferrite Sr{sub 0.7−x}Ca{sub 0.3}La{sub x}Fe{sub 12−y}Co{sub y}O{sub 19} magnets. - Highlights: • Sr{sub 0.7−x}Ca{sub 0.3}La{sub x}Fe{sub 12−y}Co{sub y}O{sub 19} hexaferrites were synthesized by the solid state reaction method. • B{sub r} continuously increases with increasing dopant contents. • H{sub cb}, H{sub cj} and (BH){sub max} for the magnets first increases and then decreases with an increase in the La–Co contents. - Abstract: Hexagonal ferrite Sr{sub 0.7−x}Ca{sub 0.3}La{sub x}Fe{sub 12−y}Co{sub y}O{sub 19} (x = 0.05–0.50; y = 0.04–0.40) magnetic powders and magnets were synthesized by the solid state reaction method. X-ray diffraction was employed to determine the phase compositions of the magnetic powders. There is a single magnetoplumbite phase in the magnetic powders with the substitution of La (0.05 ≤ x ≤ 0.15) and Co (0.04 ≤ y ≤ 0.12) contents. For the magnetic powders containing La (x ≥ 0.20) and Co (y ≥ 0.16), magnetic impurities begin to appear in the structure. A field emission scanning electron microscope was used to characterize the micrographs of the magnets. The magnets have formed hexagonal structures. Magnetic properties ofmore » the magnets were measured by a magnetic properties test instrument. The remanence continuously increases with increasing dopant contents. Whereas, the magnetic induction coercivity, intrinsic coercivity and maximum energy product for the magnets first increases and then decreases with an increase in the La–Co contents.« less
Authors:
; ; ;
Publication Date:
OSTI Identifier:
22420603
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 59; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; CALCIUM COMPOUNDS; COBALT COMPOUNDS; COERCIVE FORCE; CONCENTRATION RATIO; FERRITES; FIELD EMISSION; HEXAGONAL LATTICES; INDUCTION; LANTHANUM COMPOUNDS; MAGNETIC PROPERTIES; POWDERS; SCANNING ELECTRON MICROSCOPY; SOLIDS; STRONTIUM COMPOUNDS; SYNTHESIS; X-RAY DIFFRACTION