Structural and magnetic properties of La–Co substituted Sr–Ca hexaferrites synthesized by the solid state reaction method
Graphical abstract: The change of the remanence (B{sub r}) and intrinsic coercivity (H{sub cj}) with La content (x) and Co content (y) of hexagonal ferrite Sr{sub 0.7−x}Ca{sub 0.3}La{sub x}Fe{sub 12−y}Co{sub y}O{sub 19} magnets. - Highlights: • Sr{sub 0.7−x}Ca{sub 0.3}La{sub x}Fe{sub 12−y}Co{sub y}O{sub 19} hexaferrites were synthesized by the solid state reaction method. • B{sub r} continuously increases with increasing dopant contents. • H{sub cb}, H{sub cj} and (BH){sub max} for the magnets first increases and then decreases with an increase in the La–Co contents. - Abstract: Hexagonal ferrite Sr{sub 0.7−x}Ca{sub 0.3}La{sub x}Fe{sub 12−y}Co{sub y}O{sub 19} (x = 0.05–0.50; y = 0.04–0.40) magnetic powders and magnets were synthesized by the solid state reaction method. X-ray diffraction was employed to determine the phase compositions of the magnetic powders. There is a single magnetoplumbite phase in the magnetic powders with the substitution of La (0.05 ≤ x ≤ 0.15) and Co (0.04 ≤ y ≤ 0.12) contents. For the magnetic powders containing La (x ≥ 0.20) and Co (y ≥ 0.16), magnetic impurities begin to appear in the structure. A field emission scanning electron microscope was used to characterize the micrographs of the magnets. The magnets have formed hexagonal structures. Magnetic properties of the magnets were measured by a magnetic properties test instrument. The remanence continuously increases with increasing dopant contents. Whereas, the magnetic induction coercivity, intrinsic coercivity and maximum energy product for the magnets first increases and then decreases with an increase in the La–Co contents.
- OSTI ID:
- 22420603
- Journal Information:
- Materials Research Bulletin, Vol. 59; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure and Magnetic Properties of Ba{sub 0.95}Y{sub 0.05}Fe{sub 12−x}Co{sub x}O{sub 19} Hexaferrites
Influence of Temperature on Sr{sub 0.35}La{sub 0.40}Ca{sub .25}Fe{sub 11.6}Co{sub 0.4}O{sub 19} Hexagonal Ferrites Against Structural, Morphological and Magnetic Properties Prepared by Conventional Ceramic Reaction Methodology