Title: Structural and electrical properties of 1 − x(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–x(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} ceramics

Highlights: • We fabricated lead-free (Na{sub 0.5}K{sub 0.5})NbO{sub 3} ceramics. • We studied the structural and electrical properties of 1 − x(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–x(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} ceramics. • The structural and electrical properties improved with increasing amount of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3}. - Abstract: In this study, 1 − x(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–x(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} ceramics were fabricated using the conventional mixed oxide method. The effects of the addition of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} on the structural and electrical properties of the specimens were investigated for their application in piezoelectric devices. As the results of X-ray diffraction analysis show, all specimens display the typical polycrystalline perovskite structure without the presence of the second phase. Sintered densities increased with an increase in the amount of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} added and the specimen with 0.08 mol% of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} added showed the maximum value of 4.54 g/cm{sup 3}. Both average grain size and densification increased with an increase in the amount of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3}. The electromechanical coupling factor, dielectric constant ϵ{sub r}, dielectric loss tan δ, d{sub 33} and Curie temperature of the 0.92(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–0.08(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} specimens doped with 0.08more » mol% of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} were 0.31, 1338, 0.021, 138 and 445 °C, respectively.« less
Authors:
; ; ;
Publication Date:
OSTI Identifier:
22420576
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 58; Conference: IFFM2013: International forum on functional materials, Jeju City (Korea, Republic of), 27-29 Jun 2013; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; CALCIUM COMPOUNDS; CERAMICS; COUPLING; CURIE POINT; DOPED MATERIALS; ELECTRON MICROSCOPY; GRAIN SIZE; NIOBATES; PERMITTIVITY; PEROVSKITE; PIEZOELECTRICITY; POLYCRYSTALS; POTASSIUM COMPOUNDS; RELAXATION LOSSES; SODIUM COMPOUNDS; STRONTIUM COMPOUNDS; TITANATES; X-RAY DIFFRACTION