Title: Comparison of single junction AlGaInP and GaInP solar cells grown by molecular beam epitaxy

We have investigated ∼2.0 eV (Al{sub x}Ga{sub 1−x}){sub 0.51}In{sub 0.49}P and ∼1.9 eV Ga{sub 0.51}In{sub 0.49}P single junction solar cells grown on both on-axis and misoriented GaAs substrates by molecular beam epitaxy (MBE). Although lattice-matched (Al{sub x}Ga{sub 1−x}){sub 0.51}In{sub 0.49}P solar cells are highly attractive for space and concentrator photovoltaics, there have been few reports on the MBE growth of such cells. In this work, we demonstrate open circuit voltages (V{sub oc}) ranging from 1.29 to 1.30 V for Ga{sub 0.51}In{sub 0.49}P cells, and 1.35–1.37 V for (Al{sub x}Ga{sub 1−x}){sub 0.51}In{sub 0.49}P cells. Growth on misoriented substrates enabled the bandgap-voltage offset (W{sub oc} = E{sub g}/q − V{sub oc}) of Ga{sub 0.51}In{sub 0.49}P cells to decrease from ∼575 mV to ∼565 mV, while that of (Al{sub x}Ga{sub 1−x}){sub 0.51}In{sub 0.49}P cells remained nearly constant at 620 mV. The constant W{sub oc} as a function of substrate offcut for (Al{sub x}Ga{sub 1−x}){sub 0.51}In{sub 0.49}P implies greater losses from non-radiative recombination compared with the Ga{sub 0.51}In{sub 0.49}P devices. In addition to larger W{sub oc} values, the (Al{sub x}Ga{sub 1−x}){sub 0.51}In{sub 0.49}P cells exhibited significantly lower internal quantum efficiency (IQE) values than Ga{sub 0.51}In{sub 0.49}P cells due to recombination at the emitter/window layer interface. A thin emitter design is experimentally shown to be highlymore » effective in improving IQE, particularly at short wavelengths. Our work shows that with further optimization of both cell structure and growth conditions, MBE-grown (Al{sub x}Ga{sub 1−x}){sub 0.51}In{sub 0.49}P will be a promising wide-bandgap candidate material for high-efficiency, lattice-matched multi-junction solar cells.« less
Authors:
; ; ;  [1]
  1. Department of Electrical Engineering, Yale University, New Haven, Connecticut 06511 (United States)
Publication Date:
OSTI Identifier:
22413222
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 117; Journal Issue: 9; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ALUMINIUM COMPOUNDS; COMPARATIVE EVALUATIONS; CONCENTRATION RATIO; ELECTRIC CONTACTS; ELECTRIC POTENTIAL; GALLIUM ARSENIDES; GALLIUM COMPOUNDS; INDIUM PHOSPHIDES; INTERFACES; LAYERS; MOLECULAR BEAM EPITAXY; PHOTOVOLTAIC EFFECT; QUANTUM EFFICIENCY; RECOMBINATION; SEMICONDUCTOR JUNCTIONS; SOLAR CELLS; SUBSTRATES