Title: The role of Ag buffer layer in Fe islands growth on Ge (111) surfaces

Sub-monolayer iron atoms were deposited at room temperature on Ge (111)-c(2 × 8) substrates with and without Ag buffer layers. The behavior of Fe islands growth was investigated by using scanning tunneling microscope (STM) after different annealing temperatures. STM images show that iron atoms will cause defects and holes on substrates at room temperature. As the annealing temperature rises, iron atoms pull out germanium to form various kinds of alloyed islands. However, the silver layer can protect the Ag/Ge(111)-(√3×√3) reconstruction from forming defects. The phase diagram shows that ring, dot, and triangular defects were only found on Ge (111)-c(2 × 8) substrates. The kinds of islands found in Fe/Ge system are similar to Fe/Ag/Ge system. It indicates that Ge atoms were pulled out to form islands at high annealing temperatures whether there was a Ag layer or not. But a few differences in big pyramidal or strip islands show that the silver layer affects the development of islands by changing the surface symmetry and diffusion coefficient. The structure characters of various islands are also discussed.
Authors:
; ; ;  [1]
  1. Department of Physics, National Taiwan Normal University, 88, Sec. 4, Ting-Chou Rd, Taipei 116, Taiwan (China)
Publication Date:
OSTI Identifier:
22409978
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 117; Journal Issue: 17; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ANNEALING; CRYSTAL STRUCTURE; DIFFUSION; GERMANIUM; HOLES; IRON; LAYERS; PHASE DIAGRAMS; SCANNING TUNNELING MICROSCOPY; SILVER; SUBSTRATES; SURFACES; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0273-0400 K