Title: Enhanced magnetostrictive effect in epoxy-bonded Tb{sub x}Dy{sub 0.9−x}Nd{sub 0.1}(Fe{sub 0.8}Co{sub 0.2}){sub 1.93} pseudo 1–3 particulate composites

The spin configuration and spontaneous magnetostriction λ{sub 111} of Tb{sub x}Dy{sub 0.9−x}Nd{sub 0.1}(Fe{sub 0.8}Co{sub 0.2}){sub 1.93} (0.20 ≤ x ≤ 0.60) alloys have been investigated. The easy magnetization direction (EMD) at room temperature was observed towards the 〈111〉 axis when 0.40 ≤ x ≤ 0.60, accompanied by a rhombohedral distortion with large spontaneous magnetostriction coefficients λ{sub 111}, which increases from 1640 ppm for x = 0.40 to 1900 ppm for x = 0.60. The strong 〈111〉-oriented pseudo 1–3 particulate composite was fabricated by embedding and aligning particles in a passive epoxy matrix under an applied magnetic field. An enhanced magnetostrictive effect, the large low-field magnetostriction, λ{sub a}, as high as 480 ppm at 3 kOe, was obtained for the sample of x = 0.40, in an excess of 75% of its polycrystalline alloy although it only contains 27 vol. % alloy particles. This enhanced effect can be attributed to its low magnetic anisotropy, anisotropic magnetostrictive nature (e.g., λ{sub 111} ≠ λ{sub 100,} 〈111〉EMD), chain structure, and the 〈111〉-textured orientation. In addition, we give a direct experimental support that the 〈111〉EMD of particle and the strong 〈111〉-textured orientation are the crucial factors to realize the enhanced magnetostrictive effect in 1–3 particulate composites.
Authors:
; ; ;  [1] ;  [2]
  1. Faculty of Materials Science and Chemical Engineering, Ningbo University, Ningbo 315211 (China)
  2. Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China)
Publication Date:
OSTI Identifier:
22409938
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 117; Journal Issue: 17; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; COBALT; COMPOSITE MATERIALS; DYSPROSIUM; EPOXIDES; INTERMETALLIC COMPOUNDS; IRON; MAGNETIC FIELDS; MAGNETIZATION; MAGNETOSTRICTION; MATRIX MATERIALS; NEODYMIUM; PARTICLES; POLYCRYSTALS; TEMPERATURE RANGE 0273-0400 K; TERBIUM; TRIGONAL LATTICES