Title: Low temperature epitaxy of Ge-Sb-Te films on BaF{sub 2} (111) by pulsed laser deposition

Pulsed laser deposition was employed to deposit epitaxial Ge{sub 2}Sb{sub 2}Te{sub 5}-layers on the (111) plane of BaF{sub 2} single crystal substrates. X-ray diffraction measurements show a process temperature window for epitaxial growth between 85 °C and 295 °C. No crystalline growth is observed for lower temperatures, whereas higher temperatures lead to strong desorption of the film constituents. The films are of hexagonal structure with lattice parameters consistent with existing models. X-ray pole figure measurements reveal that the films grow with one single out-of-plane crystal orientation, but rotational twin domains are present. The out-of-plane epitaxial relationship is determined to be Ge{sub 2}Sb{sub 2}Te{sub 5}(0001) || BaF{sub 2}(111), whereas the in-plane relationship is characterized by two directions, i.e., Ge{sub 2}Sb{sub 2}Te{sub 5} [-12-10] || BaF{sub 2}[1-10] and Ge{sub 2}Sb{sub 2}Te{sub 5}[1-210] || BaF{sub 2}[1-10]. Aberration-corrected high-resolution scanning transmission electron microscopy was used to resolve the local atomic structure and confirm the hexagonal structure of the films.
Authors:
; ; ; ;  [1]
  1. Leibniz-Institut für Oberflächenmodifizierung e.V., Leipzig 04318 (Germany)
Publication Date:
OSTI Identifier:
22402399
Resource Type:
Journal Article
Resource Relation:
Journal Name: Applied Physics Letters; Journal Volume: 105; Journal Issue: 22; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ANTIMONY TELLURIDES; BARIUM FLUORIDES; ENERGY BEAM DEPOSITION; EPITAXY; FILMS; GERMANIUM COMPOUNDS; LASER RADIATION; LATTICE PARAMETERS; MONOCRYSTALS; PULSED IRRADIATION; TRANSMISSION ELECTRON MICROSCOPY; X-RAY DIFFRACTION