Title: Atomic layer deposition of tin oxide and zinc tin oxide using tetraethyltin and ozone

Silicon or glass substrates exposed to sequential pulses of tetraethyltin (TET) and ozone (O{sub 3}) were coated with thin films of SnO{sub 2}. Self-limiting deposition was found using 8 s pulse times, and a uniform thickness per cycle (TPC) of 0.2 nm/cycle was observed in a small, yet reproducible, temperature window from 290 to 320 °C. The as-deposited, stoichiometric SnO{sub 2} films were amorphous and transparent above 400 nm. Interspersing pulses of diethylzinc and O{sub 3} among the TET:O{sub 3} pulses resulted in deposition of zinc tin oxide films, where the fraction of tin, defined as [at. % Sn/(at. % Sn + at. % Zn)], was controlled by the ratio of TET pulses, specifically n{sub TET}:(n{sub TET} + n{sub DEZ}) where n{sub TET} and n{sub DEZ} are the number of precursor/O{sub 3} subcycles within each atomic layer deposition (ALD) supercycle. Based on film thickness and composition measurements, the TET pulse time required to reach saturation in the TPC of SnO{sub 2} on ZnO surfaces was increased to >30 s. Under these conditions, film stoichiometry as a function of the TET pulse ratio was consistent with the model devised by Elliott and Nilsen. The as-deposited zinc tin oxide (ZTO) films were amorphous and remained so even after annealingmore » at 450 °C in air for 1 h. The optical bandgap of the transparent ZTO films increased as the tin concentration increased. Hall measurements established that the n-type ZTO carrier concentration was 3 × 10{sup 17} and 4 × 10{sup 18} cm{sup −3} for fractional tin concentrations of 0.28 and 0.63, respectively. The carrier mobility decreased as the concentration of tin increased. A broken gap pn junction was fabricated using ALD-deposited ZTO and a sputtered layer of cuprous oxide. The junction demonstrated ohmic behavior and low resistance consistent with similar junctions prepared using sputter-deposited ZTO.« less
Authors:
;  [1] ; ;  [2]
  1. Department of Chemistry, University of Minnesota, Minneapolis, Minnesota 55455 (United States)
  2. Department of Electrical and Computer Engineering, University of Minnesota, Minneapolis, Minnesota 55455 (United States)
Publication Date:
OSTI Identifier:
22392161
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films; Journal Volume: 33; Journal Issue: 2; Other Information: (c) 2015 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ANNEALING; DEPOSITION; DEPOSITS; ELECTRIC CONTACTS; OZONE; PULSES; SEMICONDUCTOR JUNCTIONS; SPUTTERING; STOICHIOMETRY; THICKNESS; THIN FILMS; TIME PROJECTION CHAMBERS; TIN; TIN OXIDES; ZINC